Outokumpu 4529 Austenitic Stainless Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel |
| Manufacturer | Outokumpu |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Outokumpu 4529 Austenitic Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.10 g/cc | 0.293 lb/in³ | RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 750 MPa | 109000 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Tensile Strength, Yield | 300 MPa @Strain 0.200 % |
43500 psi @Strain 0.200 % |
EN min.,RT; EN 10002-1 |
| 360 MPa @Strain 0.200 % |
52200 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 | |
| 430 MPa @Strain 1.00 % |
62400 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 | |
| 160 MPa @Strain 0.200 %, Temperature 400 °C |
23200 psi @Strain 0.200 %, Temperature 752 °F |
EN min.; EN 10002-5 | |
| 190 MPa @Strain 0.200 %, Temperature 200 °C |
27600 psi @Strain 0.200 %, Temperature 392 °F |
EN min.; EN 10002-5 | |
| 230 MPa @Strain 0.200 %, Temperature 100 °C |
33400 psi @Strain 0.200 %, Temperature 212 °F |
EN min.; EN 10002-5 | |
| Elongation at Break | 55 % | 55 % | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Modulus of Elasticity | 195 GPa | 28300 ksi | RT |
| 166 GPa @Temperature 400 °C |
24100 ksi @Temperature 752 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.8 µm/m-°C @Temperature 100 °C |
8.78 µin/in-°F @Temperature 212 °F |
|
| 16.9 µm/m-°C @Temperature 400 °C |
9.39 µin/in-°F @Temperature 752 °F |
||
| Specific Heat Capacity | 0.450 J/g-°C | 0.108 BTU/lb-°F | RT |
| Thermal Conductivity | 12.0 W/m-K | 83.3 BTU-in/hr-ft²-°F | RT |
| 18.0 W/m-K @Temperature 400 °C |
125 BTU-in/hr-ft²-°F @Temperature 752 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.020 % | 0.020 % | |
| Chromium, Cr | 20 % | 20 % | |
| Copper, Cu | 0.50 % | 0.50 % | |
| Iron, Fe | 43.28 % | 43.28 % | |
| Molybdenum, Mo | 6.5 % | 6.5 % | |
| Nickel, Ni | 25 % | 25 % | |
| Nitrogen, N | 0.20 % | 0.20 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000100 ohm-cm | 0.000100 ohm-cm | RT |
Users viewing this material also viewed the following:
- Polymax® Maxelast® N8860 TPE, Nylon Overmold
- PolyOne Geon™ Vinyl Flexible B5DW2 Polyvinyl Chloride, Flexible (PVC, Flexible)
- LATI Larpeek 50 G/30 PEEK, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics ULTEM 2110EPR PEI
- SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East)
- Sharadaa Ceramics Sharada RFC-45 Gel Bonded Castables
- Samsung Cheil Industries Starex® WR-9120AT ASA, Unreinforced
- UBE UBESTA® 3030U Nylon 12 (After Water for 500 hours)
- CTC X-PRO TF 1113 HP Polypropylene Homopolymer, 13% Talc Filled
Copyright © lookpolymers.com All Rights Reserved