SABIC Innovative Plastics LNP STAT-LOY SLWM2105 PBT+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY SLWM2105 PBT+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Anti-static PBT/PC blend, mineral 5% filled product
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.015 - 0.018 cm/cm

@Thickness 3.20 mm
 0.015 - 0.018 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 30 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 30 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 20 %
20 %
Type I, 10 mm/min; SABIC - Japan Method
Elongation at Yield 20 %
20 %
Type I, 10 mm/min; SABIC - Japan Method
Tensile Modulus 2.42 GPa
351 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 77.0 MPa
11200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.410 J/cm
0.768 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 161 °C

@Thickness 3.20 mm
 322 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 9.00e+12 ohm
9.00e+12 ohm
ASTM D257