SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.740 % | 0.740 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 109 MPa | 15800 psi | ISO 527 |
| 114 MPa | 16500 psi | ASTM D638 | |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| 2.9 % | 2.9 % | ISO 527 | |
| Tensile Modulus | 7.35 GPa | 1070 ksi | 50 mm/min; ASTM D638 |
| 7.59 GPa | 1100 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 182 MPa | 26400 psi | ISO 178 |
| 186 MPa | 27000 psi | ASTM D790 | |
| Flexural Modulus | 6.41 GPa | 930 ksi | ISO 178 |
| 6.69 GPa | 970 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.13 J/cm | 7.74 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Kolon Kocetal® WH702 Reinforced Grade Acetal Copolymer (discontinued **)
- Fujipoly Industries Sarcon® 15GTR Thin-Film GTR
- Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant
- Haynes Multimet® alloy, SMAW, 3.2 mm sheet
- Teknor Apex Monprene® MP-1380A Thermoplastic Elastomer
- Universal Wire Works A356 (AMS 4181) Aluminum Alloy Filler Metal
- ELASTO UK Dryflex® 500650S SEBS Based Material, Unfilled Qualities, 65A Hardness, Translucent
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.5 PHR Varox DBPH-50 Peroxide
Copyright © lookpolymers.com All Rights Reserved