Akro-Plastic Akromid® B3 GF 30 RM-M (3016) PA 6 Dry, 30% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® B3 GF 30 RM-M (3016) PA 6 Dry, 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
In all, the construction relevant features show that the significantly reduced moisture absorption of AKROMID B3 GF 30 RM leads to increasing rigidities and strengths as already expected. Nevertheless, the viscosity features are on the level of PA6. Especially after storage, e.g. at 150° AKROMID RM shows comparable ageing characteristics. For appliances with very constant features, low warpage, very good finish together with an improved chemical resistance and for production of parts according to the GIT/WIT process, the version B3 GF 30 RM 9 black (3099) or respectively B3 GF 50 9 RM black (3147) offers an ideal solution. However, if a very good impact strength is predominant, our type B3 GF 30 RM black (3016) or respectively B3 GF 50 RM black (3146) will be favored.High quality surface finish:B3 GF 30 9 RM black (3099)/B3 GF 50 9 RM black (3147)Very constant features with regard to climateVery low warpageVery good surfaceCaCI2 resistantCost-effective:B3 GF 30 RM black (3016)/B3 GF 50 RM black (3146)Closer to PA 6 GF 30/GF 50Constant features with regard to climateLow warpageTendentious higher impact strengthTendentious higher notched impactApplications:Electronic market:e.g. sensor housings, coil former (wo.UL), plug-in connectors, plug panels etc.Automobile market:e.g. sensor housing, electrical parts, wind screen wiper bows, door handles, mirror elements, sliding roof frames etc.General mechanical engineering:e.g. control elements in printer, copier, housings of valves, pumps etc.Information from Akro-Plastic
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Filler Content 30 %
30 %
ISO 1172
Water Absorption 1.65 %

@Temperature 70.0 °C
1.65 %

@Temperature 158 °F
62% RH. Humidity; ISO 1110
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4
Spiral Flow 70.0 cm
27.6 in
7 x 4 [mm] diameter
Mechanical Properties Metric English Comments
Ball Indentation Hardness 230 MPa
33400 psi
HB 961/30; ISO 2039-1
Tensile Strength at Break 165 MPa
23900 psi
5 [mm/min]; ISO 527-2/5
Elongation at Break 2.6 %
2.6 %
5 [mm/min]; ISO 527-2/5
3.2 %
3.2 %
2 [mm/min], Flexural Strain; ISO 178
Tensile Modulus 11.0 GPa
1600 ksi
1 [mm/min]
Flexural Strength 250 MPa
36300 psi
2 [mm/min]; ISO 178
Flexural Modulus 9.60 GPa
1390 ksi
2 [mm/min]; ISO 178
Charpy Impact Unnotched 6.50 J/cm²

@Temperature -30.0 °C
30.9 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
DIN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Unannealed; ISO 75-2A
Deflection Temperature at 8.0 MPa 160 °C
320 °F
Unannealed; ISO 75-2C
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
IEC 6095-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Nozzle Temperature 240 - 280 °C
464 - 536 °F
Zone 1 225 - 300 °C
437 - 572 °F
Zone 2 225 - 300 °C
437 - 572 °F
Zone 3 225 - 300 °C
437 - 572 °F
Zone 4 225 - 300 °C
437 - 572 °F
Melt Temperature 260 - 300 °C
500 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 - 12.0 hour
4.00 - 12.0 hour
Hold Pressure 75.0 MPa
10900 psi
Back Pressure 5.00 - 10.0 MPa
725 - 1450 psi
Descriptive Properties Value Comments
Acetone Pass
100% Conc
Benzine Pass
100% Conc
Benzol Fail
100% Conc
Biodiesel Pass
50°C, 100% Conc
Brake Fluid (DOT4) Pass
130°C, 100% Conc
Pass
100% Conc
Calcium chloride, alcoholic Fail
10% Conc
Pass
10% Conc, when surface treated with 4 (chemical-stabilized)
Calcium chloride, aqueous Fail
10% Conc
Pass
10% Conc, when surface treated with 4 (chemical-stabilized)
Citric acid Pass
100% Conc
Diesel fuel (DIN 51601) Pass
100% Conc
Sulphuric acid Fail
96% Conc
Toluene Pass
100% Conc
Water Pass
100% Conc
Zinc chloride, aqueous Fail
50% Conc