Polymer Property : Tensile Modulus = 1600 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	11.0 GPa	1600 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ PC-20CF/15T Polycarbonate (PC) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Modulus	11.03 GPa	1600 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL28EG PC (Asia Pacific) LNP* Lubricomp* DFL28EG is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Milled Glass. Added features of this material include: Internally Lubricated.
Tensile Modulus	11.0 GPa	1600 ksi	ASTM D638
Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage..
Tensile Modulus	11.0 GPa	1600 ksi	5.0 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpire® KT-820 SL30 Polyetheretherketone (PEEK) (Unverified Data**) Ketaspire KT-820 SL30 is a polyetheretherketone (PEEK) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and exte..
Tensile Modulus	11.0 GPa	1600 ksi	ISO 527-1/-2
Lanxess PocanÂ® DP 7244 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, flame retardant
Tensile Modulus	11.0 GPa	1600 ksi	1 mm/min; ISO 527-1,-2
Ineos ABS LustranÂ® SAN GF30 Glass Fiber Reinforced
Tensile Modulus	11.0 GPa	1600 ksi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 216T V33 Black 1 N PA66, 33% glass fiber, DRY Description: Polyamide PA66 reinforced with 33% of glass fiber, heat stabilized, for injection molding.Available in: Asia Pacific, EuropeProduct Applications: TECHNYLÂ® A 216T V33 BLACK 1N is used..
Tensile Modulus	11.0 GPa	1600 ksi	ISO 527-1
Vyncolit A2710 Glass Fiber Reinforced Novolac Phenolic Vyncolit A2710 is a glass fiber reinforced phenolic molding compound with excellent mechanical and thermal properties.Information provided by Sumitomo Bak North America, Inc.
Tensile Modulus	11.0 GPa	1600 ksi	dry; ISO 527-1/-2
EMS-Grivory Grivory® HTV-3H1 nat PA6T/6I-GF30 Product description: Grivory HTV-3H1 natural is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I. Ac..
Tensile Modulus	11.0 GPa	1600 ksi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSG-35/4 H black 9836 PA666-GF35 Product description: Grilon TSG-35/4 H is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 35% glass fibers, modified for parts with high thermal demands. Grilon TSG-..
Tensile Modulus	11.0 GPa	1600 ksi	ISO 527-1/-2
DuPont Performance Polymers Sorona® 3030GV NC010 Polytrimethylene Terephthalate (PTT) 30% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3030GV NC010 is a 30% glass reinforced PTT resin containing 25% renewably sourced ingredients by weight (37% based on pol..
Tensile Modulus	11.0 GPa	1600 ksi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® 70G43HSLA BK099 Nylon 66 (Unverified Data**) 43% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G43HSLA BK099 is a 43% glass fiber reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont ..
Tensile Modulus	11.0 GPa	1600 ksi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BGZ-40 PA6-GF40 Product description: Grilon BGZ-40 is a normal viscosity, heat stabilized and impact modified PA 6 injection molding type with 40% glass fibers. Grilon BGZ-40 has the following important properties:..
Tensile Modulus	11.0 GPa	1600 ksi	1mm/min; ISO 527
BASF Ultramid® N-333 NF3001 33% Glass Filled PA66 (Dry) Ultramid N-333 NF3001 is a 33% glass reinforced, heat stabilized, injection molding PA66 uncolored.
Tensile Modulus	11.0 GPa @Treatment Temp. 70.0 °C, Time 936000 sec	1600 ksi @Treatment Temp. 158 °F, Time 260 hour	62% rel. humidity
Akro-Plastic Akromid® S3 GF 50 1 (3533) PA 6.10 Dry, 50% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Tensile Modulus	11.0 GPa	1600 ksi	ISO 527-2
Pasargad Polymer Peyvand Pasamid 3P-H2145B Nylon 66, 45% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co
Tensile Modulus	11.0 GPa	1600 ksi	ASTM D638
LNP Lubricomp® QFL-4036 BK8-115 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant (disconti Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..