| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | STN EN ISO 527-2 |
| Plastcom PLASTALEN® PC 69 T 10 003 Polypropylene reinforced with mineral filler Modified PP copolymer for injection molding with the content of 10% mineral filler. Application in all automotive industry. Delivered in black.Information Provided by Plastcom spol. s r.o. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | STN EN ISO 527-2 |
| Plastcom SLOVALEN PH 78 FRT 5 Polypropylene Homopolymer, Halogen Free and Phosphor Free Flame Retardant FeaturesModified homopolymer PP for injection moulding, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. Increased strength in comparison with unfil.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
| RheTech Products FT2700-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Air deflectorsFuel filler shieldsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
| Polimeri Europa Eraclene® ML 74 High Density Polyethylene - Injection Molding Eraclene ML 74 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Its narrow molecular weight distribution leads to high mechanical properties .. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO.527 DIN.53455 |
| Omnia Plastica PTFE Polytetrafluoroethylene A Fluoropolymer used mainly for its excellent chemical resistance. It has poor mechanical features. The strain, even under low weight, makes it very suitable as a gasket material.Features:Chemical: .. |
|||
| Tensile Strength at Break | <= 20.0 MPa | <= 2900 psi | ISO/R527 |
| Polykemi AB POLYfill PPC K5025 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | <= 20.0 MPa | <= 2900 psi | ISO/R527 |
| Polykemi AB POLYfill PP EVR8025H UV Polypropylene/EDPM, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ASTM D882 |
| M. Holland Company MAGMA® LL1091-K LLDPE
(discontinued **) Features: Good Heat Seal, Good Processability, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible B5DG1 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| 3M Dyneon™ THV 220A Fluorothermoplastic
(discontinued **) THV 220A is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride in the form of agglomerate. It is soluble in ketones, esters, or ether.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 2"/min; ASTM D638 |
| LyondellBasell Petrothene® GA694189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA694189 is a pelletized LLDPE copolymer resin for injection molding. Typical applications include lids and thin-walled items that require high flow and short cycle times. GA694189 exhibi.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | |
| LATI Latiblend 5262 PP Homopolymer/PA6 Blend based on Polypropylene homopolymer (PPh) / Polyamide 6 (PA6). Unfilled. High impact resistance. Very good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | |
| LATI Latilub 45/7-20T HDPE, PTFE Reinforced Self-lubricating product based on High density polyethylene (HD-PE). PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCA871 PPE-TPE (Asia Pacific) Halogen-free flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as insulation and cable jacket. Flame retardant performance and mechanical properties capable.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched LNP* LUBRICOMP* OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Teknor Apex APEX® 1017 Polyvinyl Chloride, Semi-Rigid Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molde.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | after 7days @113°C; UL 1581 |
| SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Asia Pacific) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| SCG Chemicals EL-Proâ„¢ P851JO Polypropylene Injection Molding Key Characteristics:Good processabilityHigh gloss and brightnessOdorlessSafe for food contactRecommended Applications:Clear food containerClear large size containerThin wall productsInformation prov.. |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527-2 |
| Total PSI 8350 High Impact Polystyrene 8350 is a very high impact polystyrene for extrusion. This grade has an improved environmental stress crack resistance in comparison with standard high impact grades. It is proposed for the produc.. |
|||
| Tensile Strength at Break | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
| Daikin POLYFLON M-139 PTFE Molding Powder, Free Flow Free flow powder.Processing Methods: Compression molding and automatic compression molding.Features: Excellent fluidity. Apparent density is large and ideal for automated compression molding proces.. |
|||
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ISO R 527 |
| Fainplast Compounds CKL 8318/2 Flexible PVC, Sheathing Lead Free Sheathing coaxial TV cables |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
| Ecomass® 705BI79 BaSO4 Filled ABS Nontoxic alternative to traditional materials, radiation shielding applications.Moderate Specific GravityBaSO4 Powder Filled ABSInformation provided by Technical Polymers |
|||
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ISO R 527 |
| Fainplast Compounds HL 120/1 Flexible PVC, Insulation for High Temperatures Operating temperature 110°C |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Aclo Accuguard Polypropylene HP0362V0CSL Homopolymer Flame Retardant Copper Stabilized |
|||
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ASTM D4745-11 |
| Adamas Adalon® 805 PTFE, 40% Bronze Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ASTM D4745-11 |
| Adamas Adalon® 991 PTFE Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527-2/50 |
| ExxonMobil Exxtral™ CMW 402 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive under-the-hood applications. Availability: Africa & Middle East, Asia Pacific, Europe, South America and North.. |
|||
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ISO R 527 |
| Fainplast Compounds KLT 002 Flexible PVC, Insulation Transparent Cables Lead Free Transparent cables (105°C) |
|||