SABIC Innovative Plastics LNP Thermocomp MX01767C PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MX01767C PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D 792 |
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | Type I, 5 mm/min; ASTM D 638 |
| 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 18 % | 18 % | 5 mm/min; ISO 527 |
| 25.5 % | 25.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 6.6 % | 6.6 % | 5 mm/min; ISO 527 |
| 7.5 % | 7.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.76 GPa | 255 ksi | 5 mm/min; ASTM D 638 |
| 1.76 GPa | 255 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
| Flexural Modulus | 1.49 GPa | 216 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.51 GPa | 219 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.30 J/cm @Temperature 23.0 °C |
2.44 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 14.7 J/cm @Temperature 23.0 °C |
27.5 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 141 kJ/m² @Temperature 23.0 °C |
67.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 32.0 J | 23.6 ft-lb | Multiaxial Impact; ISO 6603 |
| 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 53.0 °C @Thickness 3.20 mm |
127 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.0 ohm | 3.0 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Kazanorgsintez Ethylbenzene Fraction
- Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F)
- Shandong Rike Chemical HELIâ„¢ HG-80 PVC Processing Aid Series (PA)
- Techmer ES HiFill FR® PC FR HS GY154
- Shin-Etsu Silicones KM-907 Fluid
- Unifrax Foamfrax® Grade III Fiber Insulation
- Tra-Con Tra-Bond 526H02
- ExxonMobil Santoprene® 201-80 Thermoplastic Elastomer
- Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536
- Loctite® 3883 Stencil Print Isotropic Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved