SCG Chemicals EL-Proâ„¢ P851JO Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P851JO Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Good processabilityHigh gloss and brightnessOdorlessSafe for food contactRecommended Applications:Clear food containerClear large size containerThin wall productsInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Flexural Modulus | 1.23 GPa | 178 ksi | ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Temperature 0.000 °C |
0.735 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| 0.637 J/cm @Temperature 23.0 °C |
1.19 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 °C | 302 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 9.0 % @Thickness 1.00 mm |
9.0 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 87 % @Thickness 1.00 mm |
87 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- RheTech Products FT4802-690UVA Thermoplastic Polyolefin, UV Stabilized, HS5 Medium Dark Neutral
- SABIC Innovative Plastics Lexan® SLX1431T PC Copolymer
- ExxonMobil Optema® TC-020 Ethylene Methyl Acrylate for Extrusion Coating (discontinued **)
- NextGen Adhesives G907-08 Epoxy Adhesive
- Latrobe LSSâ„¢ D7 Tool Steel (ASTM D7)
- Teknor Apex Monprene® MP-4123 Thermoplastic Elastomer
- Universal Wire Works Waspaloy (AMS 5828) Filler Metal
- Arlon CLTE-XT High Precision Ceramic PTFE
- Ceramic Process Systems AlSiC-8, 70 vol% SiC
- Axiall 19881 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved