Aclo Accuguard Polypropylene HP0362V0CSL Homopolymer Flame Retardant Copper Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Aclo Compounders |
| Trade Name | Accuguard |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accuguard Polypropylene HP0362V0CSL Homopolymer Flame Retardant Copper Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
UL File #E99379(N) |
Users viewing this material also viewed the following:
- RheTech Products T15P100-00 12% Talc Reinforced Polypropylene, Natural
- Polimeri Europa Edistir RCL 600 Polystyrene (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000EHL Nylon 6/6 (Cond) (discontinued **)
- Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes
- Techmer ES HiFill® ABS GM30 LE 30% Glass Filled
- Hexcel® HexForce™ 1614 Fiber Glass Fabric
- A. Schulman POLYBATCH™ AO-25 Antioxidant Masterbatch Based in LDPE
- Eastman Eastman Embrace Copolyester for Shrink Film
- Nye Lubricants 2001A (SO) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved