- LyondellBasell Petrothene® GA694189 Linear Low Density Polyethylene, Injection Molding Grade
LyondellBasell Petrothene® GA694189 Linear Low Density Polyethylene, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Petrothene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Petrothene® GA694189 Linear Low Density Polyethylene, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PETROTHENE GA694189 is a pelletized LLDPE copolymer resin for injection molding. Typical applications include lids and thin-walled items that require high flow and short cycle times. GA694189 exhibits excellent flow, warp resistance and surface appearance. Specific recommendations for processing GA694189 can only be made when the processing conditions, equipment and end use are known. Contact your Equistar sales representative for more information.This product is from the former Equistar product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505 |
| Melt Flow | 140 g/10 min | 140 g/10 min | ASTM D1238 |
| Spiral Flow | 67.8 cm | 26.7 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 2"/min; ASTM D638 |
| 1% Secant Modulus | 689 MPa | 100000 psi | 0.5"/min; ASTM D790 |
| 2% Secant Modulus | 0.593 GPa | 86.0 ksi | 0.5"/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1850-7487 PBT, with carbon fiber
- Techmer ES HiFill® ABS GF60 LE 60% Glass Filled
- Silberline Sparkle Silver® Premier ET-2025
- Universal Wire Works 82 Nickel Alloy Welding Wire
- Elektro-Isola Etronax MFP G Phenolic, Cotton/synthetic Fabric Reinforcement, Black, Sheets
- EMS-Grivory Grivory® HT XE 3996 PA*-GF30
- Dow UNIPOL™ DGDA-5110 Polyolefin
- BASF Heligoen® Green K 8730 Color Additive
Copyright © lookpolymers.com All Rights Reserved