SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 5 mm/min; ISO 527 |
| 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.60 % | 0.60 % | Type I, 5 mm/min; ASTM D638 |
| 0.60 % | 0.60 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.36 GPa | 487 ksi | 1 mm/min; ISO 527 |
| 3.59 GPa | 521 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 56.0 MPa | 8120 psi | ISO 178 |
| 65.0 MPa | 9430 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.32 GPa | 482 ksi | 2 mm/min; ISO 178 |
| 3.87 GPa | 561 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.130 J/cm | 0.244 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 1.00 J @Temperature 23.0 °C |
0.738 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N2040ML Nylon 6 (DAM)
- SABIC Innovative Plastics LNP Thermocomp IF008 PA 6/12
- Styrolution PS ESCRimo HIPS
- Wanhua Chemical Wanthane® WHT-61 TPU Solvent-Based Adhesive
- A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene
- Zotefoams Plastazote® MP15FR Metallocene Polyethylene Foam, Flame Retardant
- China Tungsten ZP10-1 Tungsten Carbide
- Arlon 920-05C##FR-P1 0.020" (0.508 mm) Cured Self-fusing Silicone Tape
- A. Schulman ComAlloy Hiloy® 753 Glass Reinforced, Flow Enhanced, PPS Alloy, UL
- Mo-Sci Corporation YB-40-I Yellow B Filter Glass
Copyright © lookpolymers.com All Rights Reserved