Total PSI 8350 High Impact Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Total Atofina
Trade Name PSI
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PSI 8350 High Impact Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
8350 is a very high impact polystyrene for extrusion. This grade has an improved environmental stress crack resistance in comparison with standard high impact grades. It is proposed for the production of packaging intended for products likely to cause stress cracking, e.g. fats and oils. LACQRENE® 8350 retains good mechanical properties at low temperatures making this grade suitable for frozen packaging and for the production of fridge liners.ApplicationSheet for thermoforming and high quality printing, Cabinet and door liners for fridges, Packaging for use at low temperatures, Packaging for aggressive foodstuffs.Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines. This product was previously known as LACQRENE®
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
ISO 62
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Melt Flow 4.5 g/10 min

@Load 5.00 kg,
Temperature 200 °C
4.5 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133H
Mechanical Properties Metric English Comments
Hardness, Rockwell R 54
54
ISO 2039-2
Tensile Strength at Break 20.0 MPa
2900 psi
ISO 527-2
Tensile Strength, Yield 18.0 MPa
2610 psi
ISO 527-2
Elongation at Break 60 %
60 %
ISO 527-2
Tensile Modulus 1.60 GPa
232 ksi
ISO 527-2
Flexural Modulus 1.60 GPa
232 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear 91.0 µm/m-°C

@Temperature 20.0 °C
50.6 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
189 °F
Annealed; ISO 75-2A
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Unannealed; ISO 75-2A
Vicat Softening Point 84.0 °C
183 °F
50N (T° increase = 5°C/h); ISO 306B50
96.0 °C
205 °F
10N (T° increase = 50°C/h); ISO 306A50
Electrical Properties Metric English Comments
Surface Resistivity per Square >= 1.00e+13 ohm
>= 1.00e+13 ohm
ISO IEC93
Dielectric Strength 150 kV/mm
3810 kV/in