- Polykemi AB POLYfill PP EVR8025H UV Polypropylene/EDPM, Mineral Reinforced
Polykemi AB POLYfill PP EVR8025H UV Polypropylene/EDPM, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP EVR8025H UV Polypropylene/EDPM, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Filler Content | 25 % | 25 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
| 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 20.0 MPa | <= 2900 psi | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 30.0 MPa | <= 4350 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 70.0 °C @Load 5.001 kg |
158 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 145 °C @Load 1.00 kg |
293 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PP H6 GF25 NHFR grey Polypropylene, Unspecified (PP, Unspecified)
- SABIC Innovative Plastics Lexan® HPX4 PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics Lexan® LUX2614G PC (Europe-Africa-Middle East)
- Techmer ES HiFill® PA6/6 GF/M35 HS BK 35% Glass/Mineral Fiber Filled
- Samyang Trirex® 3030I Polycarbonate
- Techmer ES HiFill FR® PP CO FR-N V2
- CoorsTek Pure SiC™ LR CVD Silicon Carbide, > 99.9995%
- DuPont™ Nomex® 418 Paper, 3 mil Nominal Thickness
- LATI Later 4-V0 PBT, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved