Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 130 MPa | 18900 psi | STN EN ISO 178 |
Plastcom SLOVAMID 66 W 40 Polyamide 66, 40% Mineral Filled FeaturesPA 66 with the content of 40% chemically modified mineral filler. Used for grips of electric hand tools, hobby tools, gear wheels, covers of electric tools, flat products, automobile wheel .. |
|||
Flexural Strength | <= 130 MPa | <= 18900 psi | ISO 178 |
Polykemi AB POLYblend 85FS GF20 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Pyrotek TS-117 Thermoset Electrical Insulation Product (Nema Grade: GPO-1) Glass reinforcement, Polyester resin, Gray color. Economical, general purpose product.Information provided by Pyrotek. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 1105-7753/BL PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 1105-7786 PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Emergency running property.Improved wear behaviour, low warpage.High chemical resistance p.. |
|||
Flexural Strength | 130 MPa | 18900 psi | conditioned, 2 mm/min; ISO 178-A |
Lanxess Durethan® DP 2131/20 H3.0 000000 Nylon 6, 20% Glass Fiber PA 6, 20% glass fiber, injection molding, heat-ageing stabilized, weather stabilized, improved surface finishInformation provided by LANXESS. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 1106-7743 Polyether imide, with PTFE Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 1200-7116-1 ABS, with carbon fiber Applications: Office communication.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff .. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 815F PBT+PET (Europe-Africa-Middle East) PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Flexural Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® ENH4530 PBT (Europe-Africa-Middle East) 15% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp DFZ22E PC LNP* Thermocomp* DFZ22E is a compound based on Polycarbonate with Glass and Milled Fiber. Characteristics of this products is Easy Molding.This data was supplied by SABIC-IP for the Americas region.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp WF006SXC PBT LNP* Thermocomp* WF006SXC is a compound based on PBT containing Glass FIber. Characteristic of this grade is: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 130 MPa | 18900 psi | at rupture; ASTM D790 |
Sumitomo Bakelite North America Epiall® 1908-1 Short Glass Fiber Reinforced Epoxy Epiall 1908-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation proper-ties that meets the requir.. |
|||
Flexural Strength | 130 MPa | 18900 psi | Flexural Strain: 0.9%; ISO 178 |
Polyplastics Freqtis® P1210A (PPS/LCP), Molding Compound Both base resins (PPS and LCP) exhibit excellent heat resistance, dimensional stability and molding processability. Therefore Freqtis® is widely used for surface mounted electronic components. In .. |
|||
Flexural Strength | 130 MPa | 18900 psi | At Rupture; ISO 178 |
Vyncolit X620/1 Novolac Phenolic Glass fiber and graphite filled phenolic molding compound with excellent friction properties.USES: Low friction bearings, video recorder and compact disc parts. Not suitable for applications requir.. |
|||
Flexural Strength | 130 - 150 MPa | 18900 - 21800 psi | At Rupture; ISO 178 |
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Polyram Polytron P20B11 Polypropylene, 20% Long Fiber Glass A chemically coupled 20% long fiber glass reinforced black polypropylene, heat stabilized for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Polyram RamSter PF321G3 PBT, 15% Glass Fiber, Flame Retardant 15% Glass fiber reinforced, flame retardant PBT for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 130 MPa | 18900 psi | cond; ISO 178 |
DSM Novamid® 1010GN2-15Z BK701 PA6-GF15 FR(17) 15% Glass Reinforced, Flame Retardant, Easy Molding Grade, Injection Molding, High Flow |
|||
Flexural Strength | 130 - 140 MPa | 18900 - 20300 psi | ASTM D790, ISO 178 |
EPICHEM Epilon G4-PC 20% GF Polycarbonate, 20% Glass Fiber Characteristics: 20% glass fibre filled, excellent mechanical properties |
|||
Flexural Strength | >= 130 MPa | >= 18900 psi | Perpendicular to laminations; IEC 1212-2 5.1 |
Hippe UP GM 201 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet Used in mechanical and electrical applications. Good stability of electrical properties under high humidity. Good mechanical properties at moderate temperature.Information provided by Hippe. |
|||
Flexural Strength | 130 MPa | 18900 psi | Transverse direction; ISO 178 |
Azdel Plus U421B02N 42% Directionalized Continuous Fiber Mat / PP Resin Matrix AZDEL® U421B02N is a uni-directional fiber and random glass mat reinforced polypropylene composite material featuring excellent fiber distribution over long flow paths and complex part forms. This.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 125 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | <= 130 MPa | <= 18900 psi | ISO 178 |
Polykemi AB POLYfill PPH GF5035 PD2 VT Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled/Heat Resistant Information provided by Polykemi AB |
|||
Flexural Strength | >= 130 MPa | >= 18900 psi | Perpendicular to laminations; IEC 1212-2 5.1 |
Hippe UP GM 203 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet Used in mechanical and electrical applications. Good stability of electrical properties under high humidity. Good mechanical properties at moderate temperature. Flame retardant. With improved re.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ASTM D790 |
Polyram RamSter PF391G6 PBT, 30% Glass Fiber 30% glass-fiber reinforced, surface modified PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |