Sumitomo Bakelite North America Epiall® 1908-1 Short Glass Fiber Reinforced Epoxy
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | Epiall® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America Epiall® 1908-1 Short Glass Fiber Reinforced Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Epiall 1908-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation proper-ties that meets the requirements of ASTM D5948 Type GEI-5Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1895 |
| Density | 1.92 g/cc | 0.0694 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 50.0 °C, Time 173000 sec |
0.20 % @Temperature 122 °F, Time 48.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 |
| Flexural Strength | 130 MPa | 18900 psi | at rupture; ASTM D790 |
| Flexural Modulus | 15.1 GPa | 2190 ksi | ASTM D790 |
| Compressive Strength | 240 MPa | 34800 psi | ASTM D695 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.0 µm/m-°C | 20.6 µin/in-°F | ASTM E831 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL Temperature Index; UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A |
| Flammability, UL94 | V-0 @Thickness 6.40 mm |
V-0 @Thickness 0.252 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
wet; ASTM D150 |
| Dielectric Strength | 12.9 kV/mm @Frequency 60.0 Hz |
328 kV/in @Frequency 60.0 Hz |
step-by-step, wet; ASTM D149 |
| 14.3 kV/mm @Frequency 60.0 Hz |
363 kV/in @Frequency 60.0 Hz |
short time, wet; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
wet; ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Colors | Black, Blue, Green, Gray | |
| Form | Granular | |
| Molding Method | Compression | |
| Injection | ||
| Transfer |
Users viewing this material also viewed the following:
- Ovation Polymers OpteSTAT™ NC PK 8010 Polyetheretherketone based Carbon Nanotube Compound
- SABIC Innovative Plastics Lexan® EBL2061 PC (Asia Pacific)
- Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric
- Polymax® Maxelast® C4902 TPE, Transparent
- Stellarchem MP-835B TPE Compound
- A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
- Loctite® Output™ 315 Acrylic Adhesive
- Eurotec® Tecopet® PT70 GR15 NL100 PR PET, 15% glass fiber reinforced, heat stabilized, natural, fast crystallization grade
- Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Longitudinal Properties
- Aleris Alustar Aluminum Alloy, H321/H116; 20 - 40 mm thickness
Copyright © lookpolymers.com All Rights Reserved