- Lehmann & Voss LUVOCOM® 1105-7786 PEEK, with PTFE
Lehmann & Voss LUVOCOM® 1105-7786 PEEK, with PTFE
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7786 PEEK, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Emergency running property.Improved wear behaviour, low warpage.High chemical resistance parts, hydrolysis resistance, non flammable.Bearings, sleeves, sliding elements, handles, machine parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Water Absorption | <= 0.050 % | <= 0.050 % | 23°C/24h |
| Linear Mold Shrinkage | 0.010 - 0.018 cm/cm | 0.010 - 0.018 in/in | |
| Melt Flow | 21.6 g/10 min @Load 10.0 kg, Temperature 380 °C |
21.6 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 90.0 MPa | 13100 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.5 % | 6.5 % | flexural | |
| Modulus of Elasticity | 3.60 GPa | 522 ksi | |
| Flexural Strength | 130 MPa | 18900 psi | |
| Flexural Modulus | 3.00 GPa | 435 ksi | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Polycasa XT 620 PMMA
- P & P Technology Aluminum 5056 (AMS 4182) Knitted Cored Shielding Mesh
- Sharadaa Ceramics HA 62 High Alumina Brick
- Borealis SuperCOPO™ LE4205R Polyethylene Insulation Compound, Crosslinkable
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Monoplex DOS Plasticizer
- Eastman Tenite Butyrate 264E4861310 Clear, Trsp Cellulose Acetate Butyrate
- Cytec (Conap) FR-1271 Conapoxy® Resin / Conacure® Hardener
- DuPont™ Tedlar® SP TUA10AH9 Polyvinyl Fluoride Film
- Adamas Lakinor® U PVDF
- Beijing Ranger Chem SM-638 Solid Epoxy Resin