- Lehmann & Voss LUVOCOM® 1200-7116-1 ABS, with carbon fiber
Lehmann & Voss LUVOCOM® 1200-7116-1 ABS, with carbon fiber
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1200-7116-1 ABS, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Office communication.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | |
| Melt Flow | 14 g/10 min @Load 10.0 kg, Temperature 220 °C |
14 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 90.0 MPa | 13100 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 1.9 % | 1.9 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 130 MPa | 18900 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | |
| Coefficient of Friction, Static | 0.21 | 0.21 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 60.0 °C | 140 °F | |
| 80.0 °C | 176 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | |
| Vicat Softening Point | 100 °C | 212 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 - 260 °C | 446 - 500 °F | mass temp |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | |
| Zone 1 | 220 - 250 °C | 428 - 482 °F | |
| Zone 2 | 220 - 250 °C | 428 - 482 °F | |
| Zone 3 | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 95.0 °C @Time 7200 - 14400 sec |
158 - 203 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- MV Labs PT855 K2PtCl4 Potassium tetrachloroplatinate(II)
- Premix Premi-Glas® 1240-25 Fiberglass Reinforced Thermoset Thick Molding Compound
- SABIC Innovative Plastics LNP STAT-KON EEF42 PEI
- Silberline EternaBrite® Premier 251-PA
- Solvay DURAPHOS® 100 Octadecyl phosphonate
- Borealis BC612WG Polypropylene Copolymer
- Tipco Tipcolene® X 408 IN - 10% Talc/Mineral Reinforced Polypropylene Copolymer, Very High Impact Strength & Flow
- Arkema Group Orgalloy® RS 60E10TL Nylon 6 Alloy, Rigid Grade (Conditioned)
- ChevronTexaco ISO 22 Hydraulic Oil AW
Copyright © lookpolymers.com All Rights Reserved