DSM Novamid® 1010GN2-15Z BK701 PA6-GF15 FR(17)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1010GN2-15Z BK701 PA6-GF15 FR(17).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass Reinforced, Flame Retardant, Easy Molding Grade, Injection Molding, High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.00 % | 2.00 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 118 MPa | 17100 psi | dry; ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| Flexural Strength | 130 MPa | 18900 psi | cond; ISO 178 |
| 175 MPa | 25400 psi | dry; ISO 178 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | cond; ISO 178 |
| 6.00 GPa | 870 ksi | dry; ISO 178 | |
| Charpy Impact, Notched | 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | dry; ISO 75-1/-2 |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials PEARLCOAT® 126K Thermoplastic Polyurethane Elastomer (discontinued **)
- Johnson Matthey SC 850 Platinum w/ 15% Palladium Jewelry Alloy
- Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F)
- Styron EMERGEâ„¢ 4630-10 Polycarbonate
- Techmer ES HiFill FR® PP CO E FR
- Universal Wire Works A Nickel Alloy Welding Wire
- Wico Plast Wicotal 270 Acetal
- Tra-Con Tra-Bond 77-1S One Component SMD Adhesive
- Loctite® FASTGASKET® 5950 Flange Sealant
Copyright © lookpolymers.com All Rights Reserved