Azdel Plus U421B02N 42% Directionalized Continuous Fiber Mat / PP Resin Matrix

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Azdel
Trade Name	Plus
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azdel Plus U421B02N 42% Directionalized Continuous Fiber Mat / PP Resin Matrix.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AZDEL® U421B02N is a uni-directional fiber and random glass mat reinforced polypropylene composite material featuring excellent fiber distribution over long flow paths and complex part forms. This material allows highly directionalized reinforcement where loads are in defined planes.The material can be combined with AZDEL random mat products to reinforce localized high stress paths, minimizing both part weight and cost.Commercially available only to European based customers.Information provided by Azdel.

Physical Properties	Metric	English	Comments
Specific Gravity	1.21 g/cc	1.21 g/cc	Laminate; ISO 2577
	1.25 g/cc	1.25 g/cc	Molded plaque; ISO 2577
Filler Content	42 %	42 %	AZDEL Test
Thickness	3900 microns	154 mil	AZDEL Test
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	flat plaques, 320 x 320 mm; ISO 1183
Linear Mold Shrinkage, Transverse	0.0040 cm/cm	0.0040 in/in	measured on flat plaques, 320 x 320 mm; ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 MPa	7250 psi	Transverse direction; ISO 527/4
	270 MPa	39200 psi	Longitudinal direction; ISO 527/4
Elongation at Break	2.0 %	2.0 %	Transverse direction; ISO 527/4
	2.4 %	2.4 %	Longitudinal direction; ISO 527/4
Tensile Modulus	4.20 GPa	609 ksi	Transverse direction; ISO 527/4
	12.5 GPa	1810 ksi	Longitudinal direction; ISO 527/4
Flexural Strength	130 MPa	18900 psi	Transverse direction; ISO 178
	270 MPa	39200 psi	Longitudinal direction; ISO 178
Flexural Modulus	5.00 GPa	725 ksi	Transverse direction; ISO 178
	9.00 GPa	1310 ksi	Longitudinal direction; ISO 178
Charpy Impact, Notched	6.00 J/cm²	28.6 ft-lb/in²	Transverse direction; ISO 179/2fn
	18.0 J/cm²	85.7 ft-lb/in²	Longitudinal direction; ISO 179/2fn
Impact	13300 @Thickness 4.00 mm	13300 @Thickness 0.157 in	Multi-axial in Newtons, at max. force; ISO 6603-2
Impact Test	58.0 J @Thickness 4.00 mm	42.8 ft-lb @Thickness 0.157 in	Multi-axial, at max. force; ISO 6603-2
	100 J @Thickness 4.00 mm	73.8 ft-lb @Thickness 0.157 in	Multi-axial, total energy; ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear	17.0 µm/m-°C @Temperature 0.000 - 120 °C	9.44 µin/in-°F @Temperature 32.0 - 248 °F	longitudinal direction, 100 x 15 x 3 mm sample; AZDEL Test
	27.0 µm/m-°C @Temperature -30.0 - 0.000 °C	15.0 µin/in-°F @Temperature -22.0 - 32.0 °F	longitudinal direction, 100 x 15 x 3 mm sample; AZDEL Test
	33.0 µm/m-°C @Temperature 0.000 - 120 °C	18.3 µin/in-°F @Temperature 32.0 - 248 °F	longitudinal direction, 100 x 15 x 3 mm sample; AZDEL Test
CTE, linear, Transverse to Flow	50.0 µm/m-°C @Temperature -30.0 - 0.000 °C	27.8 µin/in-°F @Temperature -22.0 - 32.0 °F	100 x 15 x 3 mm sample; AZDEL Test
Melting Point	119 °C	246 °F	Recrystallizing temperature; ISO 3146
	166 °C	331 °F	ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	145 °C	293 °F	Transverse direction; ISO 75/2a
	160 °C	320 °F	Longitudinal direction; ISO 75/2a

Processing Properties	Metric	English	Comments
Processing Temperature	205 - 220 °C	401 - 428 °F	Surface temperature
Mold Temperature	30.0 - 90.0 °C	86.0 - 194 °F
Back Pressure	15.0 - 25.0 MPa	2180 - 3630 psi	Depending on wall thickness and part complexity