Polykemi AB POLYblend 85FS GF20 PC/ABS-Blend, Glass Fiber reinforced

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer Polykemi AB
Trade Name POLYblend
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYblend 85FS GF20 PC/ABS-Blend, Glass Fiber reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Filler Content 20 %
20 %
±2%; Polykemi
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
With Flow; ISO 2577
0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Across Flow; ISO 2577
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Elongation at Yield 2.5 %
2.5 %
ISO/R527
Flexural Strength <= 130 MPa
<= 18900 psi
ISO 178
Flexural Modulus 5.90 GPa

@Temperature 23.0 °C
 856 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.600 J/cm²

@Temperature -20.0 °C
 2.86 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
120°C/h; ISO 75/1
Vicat Softening Point 135 °C

@Load 5.001 kg
 275 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 100 - 110 °C
212 - 230 °F
Dry Time 2 - 8 hour
2 - 8 hour
in circulation dryer
2 - 8 hour
2 - 8 hour
in fresh-air dryer
2 - 8 hour
2 - 8 hour
in desiccant air dryer
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi
Back Pressure 0.500 - 1.50 MPa
72.5 - 218 psi
Descriptive Properties Value Comments
Holding Pressure () 20-50
% of injection pressure
Injection Speed () High
Users viewing this material also viewed the following: