- Polyram RamSter PF321G3 PBT, 15% Glass Fiber, Flame Retardant
Polyram RamSter PF321G3 PBT, 15% Glass Fiber, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF321G3 PBT, 15% Glass Fiber, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass fiber reinforced, flame retardant PBT for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ISO 2577 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 105 MPa | 15200 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.20 kJ/m² | 3.43 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Glow Wire Test | 960 °C | 1760 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CX2244ME PC+ABS (Europe-Africa-Middle East)
- SABIC Innovative Plastics PC1800 PC (Asia Pacific)
- Alliance N-50 Neodymium Iron Boron Magnetic Material
- E-Polymers TEKALOY® G75NHT Brominated Flame Retardant High Impact PC/ABS Alloy
- Gouda Vuurvast CURON 185 T Dense Refractory Castable
- SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1301-8212/BL PPS, linear, with glass fiber and PTFE
- DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved