SABIC Innovative Plastics Valox® 815F PBT+PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 815F PBT+PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | ASTM D229 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.26 % | 0.26 % | ISO 62 |
| Viscosity | 160000 cP | 160000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm |
0.0040 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 266 °C |
16 g/10 min @Load 2.65 lb, Temperature 511 °F |
ASTM D1238 |
| 70 g/10 min @Load 5.00 kg, Temperature 266 °C |
70 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 | |
| 70 g/10 min @Load 5.00 kg, Temperature 265 °C |
70 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 12 g/10 min @Load 1.20 kg, Temperature 265 °C |
12 g/10 min @Load 2.65 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 22 g/10 min @Load 5.00 kg, Temperature 250 °C |
22 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 50 g/10 min @Load 5.00 kg, Temperature 265 °C |
50 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ISO 2039-2 |
| Hardness, H358/30 | 195 MPa | 28300 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 5.0 % | 5.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.50 GPa | 798 ksi | 5 mm/min; ASTM D638 |
| 5.50 GPa | 798 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.10 GPa | 740 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| 0.390 J/cm @Temperature 0.000 °C |
0.731 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.390 J/cm @Temperature -30.0 °C |
0.731 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 3.00 J/cm | 5.62 ft-lb/in | ASTM D4812 |
| 3.00 J/cm @Temperature -30.0 °C |
5.62 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature 0.000 °C |
1.90 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/2C |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/2C |
| 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
30.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 195 °C | 383 °F | Rate B/120; ISO 306 |
| 197 °C | 387 °F | Rate B/50; ISO 306 | |
| 197 °C | 387 °F | Rate B/50; ASTM D1525 | |
| 220 °C | 428 °F | Rate A/50; ISO 306 | |
| 220 °C | 428 °F | Rate A/50; ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200-10 Fiberglass Reinforced Thermoset SMC
- GEHR Plastics PP-30GF Polypropylene, 30% Glass Fiber
- Solvay TECHNYLSTARâ„¢ A205 F Natural S PA6, Eh 0
- Techmer ES Plastiblend® TPX-HTN-000AB 15% Glass Filled
- Silberline Sparkle Silvet® Premier 890-30-E1
- Chosun Refractories AB10H Alumina Magnesia Carbon Bricks for Ladle Wall And Bottom
- Teijin Panlite® G-3420R Glass Fiber Reinforced Polycarbonate Resin
- LG Chemical XR401F ABS, Heat Resistance
- Borealis Borstar® ME3444 Blue Medium Density Polyethylene for Drinking Water Pipes
Copyright © lookpolymers.com All Rights Reserved