SABIC Innovative Plastics LNP Thermocomp WF006SXC PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp WF006SXC PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* WF006SXC is a compound based on PBT containing Glass FIber. Characteristic of this grade is: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D 792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.040 % @Time 86400 sec |
0.040 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 |
| 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| 8.83 GPa | 1280 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| 136 MPa | 19700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 7.82 GPa | 1130 ksi | 2 mm/min; ISO 178 |
| 8.04 GPa | 1170 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C |
0.693 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.56 J/cm @Temperature 23.0 °C |
6.67 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- MV Labs YB700 Yb(NO3)3·5H2O Ytterbium nitrate pentahydrate
- Nye Lubricants 880FG (FG) Synthetic Oil
- Overview of materials for Polycarbonate, Foam Grade, Glass Filled
- SABIC Innovative Plastics LNP STAT-LOY M3000 PP (Europe-Africa-Middle East)
- ChevronTexaco 250 NC Open Gear Lubricant
- DuPont Performance Polymers Crastin® 6134 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- ChevronTexaco Starplex® NLGI Grade 1
- China Tungsten ZP35 Tungsten Carbide
- DuPont Teijin Films Mylar® WC Polyester Film, 500 Gauge
Copyright © lookpolymers.com All Rights Reserved