SABIC Innovative Plastics Valox® ENH4530 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® ENH4530 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | ASTM D229 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Viscosity | 150000 cP | 150000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 24 g/10 min @Load 5.00 kg, Temperature 265 °C |
24 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 265 °C |
17 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 18 g/10 min @Load 5.00 kg, Temperature 250 °C |
18 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ISO 2039-2 |
| Hardness, H358/30 | 128 MPa | 18600 psi | ISO 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 3.0 % | 3.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 5 mm/min; ASTM D638 |
| 7.50 GPa | 1090 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 130 MPa | 18900 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 130 MPa | 18900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 5.80 GPa | 841 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.40 GPa | 928 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| 0.500 J/cm @Temperature 0.000 °C |
0.937 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.500 J/cm @Temperature -30.0 °C |
0.937 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D4812 |
| 3.60 J/cm @Temperature -30.0 °C |
6.74 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature 0.000 °C |
2.86 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 23.0 kJ/m² @Temperature -30.0 °C |
10.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/2C |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/2C |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 42.0 µm/m-°C @Temperature 23.0 - 150 °C |
23.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 173 µm/m-°C @Temperature 23.0 - 150 °C |
96.1 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 205 °C | 401 °F | Rate B/50; ASTM D1525 |
| 205 °C | 401 °F | Rate B/50; ISO 306 | |
| 205 °C | 401 °F | Rate B/120; ISO 306 | |
| 217 °C | 423 °F | Rate A/50; ASTM D1525 | |
| 220 °C | 428 °F | Rate A/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 21.0 kV/mm @Thickness 1.60 mm |
533 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 21.0 kV/mm @Thickness 1.60 mm |
533 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 28.0 kV/mm @Thickness 0.800 mm |
711 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| 28.0 kV/mm @Thickness 0.800 mm |
711 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.15 @Frequency 1.00e+6 Hz |
0.15 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.15 @Frequency 1.00e+6 Hz |
0.15 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K 2x2 Twill Reinforced
- Gharda Chemicals Gafone™ 3100 Polyethersulfone (PES) (discontinued **)
- Cookson Group Plaskon® 440 Mineral Filled Novolac Epoxy Molding Compound (discontinued **)
- MarkeTech Lutetium Aluminum Garnet:Cerium (LAG:Ce) Scintillator Crystal
- Indium Corp. Indalloy 177 Gold-Indium Solder Alloy
- Schott GM39923 Dental Glass
- Spartech Polypedic A Low Density Polyethylene
- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
- Lubrizol ESTANE® 58810 Ether Based Thermoplastic Polyurethane
- Lucobit Lucobit® 1235 Ethylene Copolymer Bitumen
Copyright © lookpolymers.com All Rights Reserved