Total PPC 12642 Polypropylene, Heterophasic Copolymer, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Total Atofina |
| Trade Name | PPC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPC 12642 Polypropylene, Heterophasic Copolymer, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene PPC 12642 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 70 g/10 min and good mechanical properties.Polypropylene PPC 10641 has been developed for high speed injection molding of thin walled packaging containers.Peroxide is not used in the manufacturing of this product.Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ISO 1183 |
| Bulk Density | 0.525 g/cc | 0.0190 lb/in³ | ISO 1183 |
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ISO 2039-2 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527-2 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
ISO 180 |
| 6.50 kJ/m² @Temperature 2.00 °C |
3.09 ft-lb/in² @Temperature 35.6 °F |
ISO 180 | |
| Charpy Impact, Notched | 0.450 J/cm² @Temperature -20.0 °C |
2.14 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C per hour; ISO 752 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C per hour; ISO 752 |
| Vicat Softening Point | 80.0 °C @Load 5.10 kg |
176 °F @Load 11.2 lb |
50°C per hour; ISO 306 |
| 148 °C @Load 1.02 kg |
298 °F @Load 2.25 lb |
50°C per hour; ISO 306 |