Polymer Property : Tensile Strength, Yield = 3920 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527-2
Polyplastic Armlen® PP MF 20-2HS-901 Polypropylene, 20% Mineral Filled Heat stabilized, black colored, HVAC applicationsInformation provided by PolyPlastic Group.
Tensile Strength, Yield	>= 27.0 MPa	>= 3920 psi	ASTM D638
NIZHNEKAMSKNEFTEKHIM PP 4132B (PA14D) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates very high long-term thermal stability, thermal-oxidative degradation r..
Tensile Strength, Yield	27.0 - 135 MPa	3920 - 19600 psi	Average value: 47.0 MPa Grade Count:34
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m..
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
Polimeri Europa Eraclene® MS 80 High Density Polyethylene - Injection Molding Eraclene MS 80 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MS 80 shows a good balance between processability and mechanical pro..
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min
Polimeri Europa EDISTIR RC3 High Impact Polystyrene (HIPS) (discontinued **) Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,M,088-06-07-18 Special high impact, high gloss polystyrene grade. Suitable for injection molding in the appliances sector..
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
Total Finathene® 53140 HDPE, blow molding, sheet (discontinued **) Finathene® 53140 is a high density polyethylene produced by the slurry loop low pressure polymerization process FINATHENE® 53140 has been especially developed for the manufacturing of blow molded ..
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
Global R-1760 High Density Polyethylene, Injection Molding Grade (discontinued **) Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- auto parts, bottles, housewares, drums, containers, bottlesMeets FDA requirements as listed in..
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
BP Amoco Acctuf® 3045 Impact Copolymer Polypropylene (discontinued **) Suggested fabrication methods: Extrusion; Compression; Injection moldingFeatures: Medium-term heat aging; UL recognizedComplies with FDA specification, Title 21, CFR 177.1520.Typical property data ..
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
GEHR Plastics PE-HD Polyethylene HDPE Polyethylene has a good chemical resistance against almost all acids and bases, detergents and hot water. PE has good insulation properties and is easy to weld. The operating temperature is from -50..
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 2-3120 20% Talc Filled Polypropylene Block-Copolymer INNOPOLÂ® CS 2-3120 is a 20% talc filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-3120 is developed for producing..
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 2-9000 MA B Polypropylene Copolymer INNOPOLÂ® CS 2-9000 MA B is a black colored, high melt flow copolymer with antistatic additive.INNOPOLÂ® CS 2-9000 MA B is developed for producing injection molded automotive components.All info..
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638-02
Ipiranga Petrochem GP 9452 F HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Tensile Strength, Yield	27.0 MPa	3920 psi	BP 13B/1
SIDPEC EGYPTENEÂ® HD 5218 EA HDPE Injection Molding Applications:House waresThin-walled food containersPET bottle base cupInformation provided by Interchim s.r.l., official distributor of Sidi Kerir Petrochemicals Co. (SIDPEC) Products
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
Styrolution PS 476L HIPS Styrolution PS 476L is a normal flow and very high impact Polystyrene. It gives good mechanical and heat resistance properties while providing with easy processability and short cycle time.Normal fl..
Tensile Strength, Yield	27.0 MPa	3920 psi	BP 13B/1
SIDPEC EGYPTENEÂ® HD 5740 UA HDPE Injection Molding Applications:Large dustbins and pailsPallet boxesFish cratesTechnical moldingInformation provided by Interchim s.r.l., official distributor of Sidi Kerir Petrochemicals Co. (SIDPEC) Products
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact.
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
Teknor Apex Sinpolene CPP2020 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Calcium Carbonate Filler, 20% Filler by Weight Features: Copolymer Uses: Furniture Forms: PelletsInformation Provided ..
Tensile Strength, Yield	27.0 MPa	3920 psi	50mm/min; ISO 527-2
Borealis RG460MO Polypropylene, Transparent Random Copolymer RG460MO is a specially modified transparent polypropylene random copolymer with high melt flow. and is designed for high-speed injection molding and contains nucleating and demolding additives. Pro..
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
Unipetrol PE HD LITEN® VB 33 HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene DescriptionPolyflam® RPP 1021 is a general purpose copolymer polypropylene flame retardant material with a UL V-2 flammability rating and 105°C temperature index at 0.030 in.Information provided b..
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman.
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527-2
Total PPC 10641 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 10641 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 44 g/10 min.Polypropylene PPC 10641 is characterized by high fluidity with good mechanical prope..
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene DescriptionPolyflam® RPP 1021 is a general purpose copolymer polypropylene flame retardant material with a UL V-2 flammability rating and 105°C temperature index at 0.030 in.Information provided b..
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200X is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min, 4 mm; ISO 527
Chi Mei Kibiton® PB-5903 SBC High transparency, high toughness, PS Impact modifier
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
3D Systems DuraForm® GF Glass Filled Nylon For use with all selective laser sintering (SLS®) systems.ApplicationsHousings and enclosuresConsumer sporting goodsAppropriate for low- to mid-volume rapid manufacturingParts requiring machining o..
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min
Arkema Group Rilsan® BESN P40 TL Nylon 11, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA11-P,EHL,22-003Flexible grade for tubes extrusion. Available color: black and natural. Light and heat stabilized.High flexibility. High impact strength. Very good chemical res..
Tensile Strength, Yield	27.0 MPa	3920 psi
BASF Polystyrol® 455 F WU Impact Grade Polystyrene (Europe) Very easy-flowing, impact-modified grade.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman.