Total HDPE HL 717 High Density Polyethylene - Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Total Atofina
Trade Name	HDPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total HDPE HL 717 High Density Polyethylene - Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HDPE HL 717 is a high density polyethylene produced by the gas phase polymerization process with hexene as a comonomer.HDPE HL 717 is a monomodal HDPE with a broad molecular weight distribution. It is characterized by a good melt strength and a low gel content.HDPE HL 717 is a grade to be used for thin films requiring high rigidity and high heat resistance.HDPE HL 717 can be processed on most HD-, LD-, and LLDPE blown film equipment.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.958 g/cc	0.958 g/cc	ISO 1183
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
	22 g/10 min @Load 21.6 kg, Temperature 190 °C	22 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	34.0 MPa	4930 psi	ISO 527-3
Film Tensile Strength at Yield, TD	31.0 MPa	4500 psi	ISO 527-3
Film Elongation at Break, MD	290 %	290 %	ISO 527-3
Film Elongation at Break, TD	480 %	480 %	ISO 527-3
Flexural Modulus	1.30 GPa @Strain <=0.250 %	189 ksi @Strain <=0.250 %	ISO 178
Elmendorf Tear Strength, MD	0.500 g/micron	12.7 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	8.40 g/micron	213 g/mil	ISO 6383-2
Dart Drop Test	75.0 g	0.165 lb	ISO 7765-1
Film Tensile Strength at Break, MD	66.0 MPa	9570 psi	ISO 527-3
Film Tensile Strength at Break, TD	56.0 MPa	8120 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	135 °C	275 °F	ISO 11357
Vicat Softening Point	132 °C	270 °F	ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	190 - 220 °C	374 - 428 °F