Physical Properties	Metric	English	Comments
Melt Flow	0.30 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 - 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled Information provided by PolyPlastic Group.
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 190 °C	0.30 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Eraclene® FA 706 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion Eraclene FA 706 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Films manufactured with Eraclene FA 706 show good processability t..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Eraclene® FC 82 High Density Polyethylene - Blown Film Extrusion Eraclene FC 82 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully co..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Premix Thermoplastics PRE-ELEC® PP 1373 PRE-ELEC PP 1373 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Premix Thermoplastics PRE-ELEC® PP 1385 PRE-ELEC PP 1385 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE..
Melt Flow	0.30 - 0.50 g/10 min @Load 5.00 kg, Temperature 190 °C	0.30 - 0.50 g/10 min @Load 11.0 lb, Temperature 374 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 6250D (506H4) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow	0.30 - 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 - 0.50 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PP 8332C (EPD60R) Propylene and Ethylene Block Polymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
DSM Arnitel® EB500 Polyether Ester Elastomer (European and Asian Grade) (discontinued **) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
SABIC B5429/B5429A High Density Polyethylene for Blow Molding Product Description: B5429 Series grades are medium molecular weight High Density Polyethylene copolymer. They are primarily intended for blow molding articles of small sizes. B5429 series grades..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
SABIC PP 651H Polypropylene Random Copolymer for PIPE Product Description: PP 651H is specially designed for transport of hot and cold drinking water. This grade is highly heat stabilized and specially formulated for extraction resistance.Typical App..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Premix Thermoplastics PRE-ELEC® PE 1304 (discontinued **) PRE-ELEC PE 1304 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi..
Melt Flow	0.30 g/10 min @Load 2.16 kg	0.30 g/10 min @Load 4.76 lb	ISO 1133
Total Finathene® 6002 HDPE, blow molding, pipe (discontinued **) FINATHENE® 6002 is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® 6002 has been especially developed for the manufacturing of toys and of b..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis BE50-7032 Polypropylene Homopolymer for Non-Pressure pipes and extruded sheets BE50-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer characterized by high stiffness, high heat distortion temperature and high resistance to thermal aging. The materia..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis BEC5012 Polypropylene Block Copolymer for Non-Pressure Pipes BEC5012 is a high molecular weight, low flow rate polypropylene block copolymer with very high impact strength. Applications: BEC5012 is recommended for non-pressure pipes and fittings, structured..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Beta (ß)-PP™ BE60-7032 Grey Polypropylene Homopolymer for Pressure Pipes, Fittings and Sheets Beta(ß)-PP BE60-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer with fine grained ß-modification crystalline structure leading to excellent impact strength even at lo..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis Borstar® FB3450 HDPE for Film Extrusion Borstar® FB3450 is a high density polyethylene. Borstar® FB3450 is well suited for multilayer coextruded films where higher stiffness and toughness than in standard LDPE and LLDPE is required. Ap..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis BS2581 High Density Polyethylene for Blow Molding BS2581 is a high density polyethylene intended for blow molding products with high stiffness and very good environmental stress crack resistance (ESCR). Applications: industrial chemicals, househol..
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 190 °C	0.30 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Borealis FS1560 High Density Polyethylene FS1560 is a high density polyethylene film grade which combine excellent extrusion behavior with superior mechanical properties. Films made of FS1560 have high impact and tensile strength, and bala..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Total HDPE HL 717 High Density Polyethylene - Blown Film HDPE HL 717 is a high density polyethylene produced by the gas phase polymerization process with hexene as a comonomer.HDPE HL 717 is a monomodal HDPE with a broad molecular weight distribution. It..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis BS2541 High Density Polyethylene BS2541 is a high density polyethylene with very high ESCR This product is intended for blow molding. Applications: household and chemical containers such as detergents, cleaners, and motor oils, an..
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Chi Mei Polylac® PA-747R ABS - Extrusion Attach case and refrigerator
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ExxonMobil Method
ExxonMobil Pax-Plus™ 3204 Blown Film Resin Pax-Plus 3204 is a rubber modified high density polyethylene film resin which is used primarily in film requiring good impact strength. It is specially formulated to provide easy tear in the machin..
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A Condition G; ASTM D1238
Diamond Polymers ASA T-115 Description: ASA Weatherable Polymer, Injection Molding Grade, High Heat ResistanceInformation provided by Diamond Polymers, Inc.
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A; ASTM D1238
Diamond Polymers ASA TW-18B1 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High HeatInformation provided by Diamond Polymers, Inc.
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A; ASTM D1238
Diamond Polymers ASA TW-18B2 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High HeatInformation provided by Diamond Polymers, Inc.
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A Condition G; ASTM D1238
Diamond Polymers ASA TW-20 Description: ASA Weatherable Polymer, Injection Molding Grade, High HeatInformation provided by Diamond Polymers, Inc.
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Chi Mei Polylac® PA-747F ABS - Extrusion Refrigerator
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 200 °C	0.30 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Diamond Polymers DIAMALOY VP22 NATURAL 1001B Blow Molding Grade, Flame Retardant ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	0.30 g/10 min @Load 5.00 kg, Temperature 190 °C	0.30 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Total XSene® HD55110 High Density Polyethylene - Blown Film HDPE HD55110 is a bimodal high density polyethylene with a particular molecular design developed with Total Petrochemicals Double Loop Technology™.HDPE HD55110 has been especially designed for appl..
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis Bormed™ HE2581-PH HDPE for Healthcare Applications Bormed HE2581-PH is a high-density polyethylene intended for blow molding of products with high stiffness and very good environmental stress crack resistance (ESCR). Bormed HE2581-PH can as well be ..