Total Finathene® 2344 HDPE film  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Finathene® 2344 HDPE film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Trash can liners, merchandise bags, deli wrapInformation provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.946 g/cc
0.0342 lb/in³
ASTM D 792
Water Vapor Transmission 15.5 g/m²/day
0.998 g/100 in²/day
100°F; E 96/66
Thickness 20.3 microns
0.800 mil
Melt Flow 0.080 g/10 min

@Load 2.16 kg
0.080 g/10 min

@Load 4.76 lb
ASTM D 1238
0.34 g/10 min

@Load 5.00 kg
0.34 g/10 min

@Load 11.0 lb
ASTM D 1238
High Load Melt Index 9.0 g/10 min

@Load 21.6 kg
9.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD >= 34.5 MPa
>= 5000 psi
ASTM D 882 A
Film Tensile Strength at Yield, TD >= 33.1 MPa
>= 4800 psi
ASTM D 882 A
Film Elongation at Break, MD 300 - 500 %
300 - 500 %
ASTM D 882 A
Film Elongation at Break, TD 300 - 500 %
300 - 500 %
ASTM D 882 A
Secant Modulus, MD 0.758 GPa
110 ksi
ASTM D 882 A
Secant Modulus, TD 0.841 GPa
122 ksi
ASTM D 882 A
Elmendorf Tear Strength MD 26 g
26 g
ASTM D 1922
Elmendorf Tear Strength TD 120 g
120 g
ASTM D 1922
Dart Drop Test 350 g
0.772 lb
ASTM D 1709
Film Tensile Strength at Break, MD >= 58.6 MPa
>= 8500 psi
ASTM D 882 A
Film Tensile Strength at Break, TD >= 55.8 MPa
>= 8100 psi
ASTM D 882 A
Thermal Properties Metric English Comments
Melting Point 126 °C
258 °F
ASTM D3417