AGY ZenTron® S-2 Generic S-Glass Fiber
| Category | Ceramic , Glass , Glass Fiber , Other Engineering Material , Composite Fibers |
| Manufacturer | AGY Holding Corp. |
| Trade Name | ZenTron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AGY ZenTron® S-2 Generic S-Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
S-2 glass and S-glass have the same composition. S-glass is no longer made by AGY, but used to have a reactive epoxy size. Various silanes and starch oil are used as binders. Acid resistant. Moderate alkali resistance.Information provided by AGY Holding Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.48 g/cc | 0.0896 lb/in³ | |
| Density | 2.46 g/cc | 0.0889 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % | |
| Loss On Ignition | 0.10 - 1.4 % | 0.10 - 1.4 % | Varies according to size type |
| Filament Diameter | 5.0 - 25 µm | 5.0 - 25 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 4445 MPa @Temperature 371 °C |
644700 psi @Temperature 700 °F |
|
| 4890 MPa @Temperature 23.0 °C |
709000 psi @Temperature 73.4 °F |
||
| Elongation at Break | 5.7 % | 5.7 % | in 50 mm |
| Modulus of Elasticity | 86.9 GPa | 12600 ksi | |
| Poissons Ratio | 0.22 | 0.22 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 1.60 µm/m-°C @Temperature -30.0 - 250 °C |
0.889 µin/in-°F @Temperature -22.0 - 482 °F |
average, isotropic |
| Specific Heat Capacity | 0.737 J/g-°C @Temperature 23.0 °C |
0.176 BTU/lb-°F @Temperature 73.4 °F |
|
| 0.935 J/g-°C @Temperature 200 °C |
0.223 BTU/lb-°F @Temperature 392 °F |
||
| Thermal Conductivity | 1.10 - 1.40 W/m-K | 7.63 - 9.72 BTU-in/hr-ft²-°F | |
| Melting Point | 1466 °C | 2671 °F | Liquidus |
| Liquidus | 1466 °C | 2671 °F | |
| Maximum Service Temperature, Air | 875 °C | 1610 °F | Well above Tg, due to reversible phase separation |
| Maximum Service Temperature, Inert | 875 °C | 1610 °F | |
| Transformation Temperature, Tg | 845 °C | 1550 °F | |
| Softening Point | 1056 °C | 1933 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.521 | 1.521 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 9.05e+12 ohm-cm | 9.05e+12 ohm-cm | |
| Dielectric Constant | 5.2 @Frequency 1e+10 Hz |
5.2 @Frequency 1e+10 Hz |
|
| 5.3 @Frequency 1e+6 Hz |
5.3 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | |
| Dissipation Factor | 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear |