Solvay TECHNYL® A 30 H1 V30 PA66, 30% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 30 H1 V30 PA66, 30% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 30H1 V30 is a brominated flame retardant polyamide 66, reinforced with 30% of glass fiber, for injection molding. This product is available in natural & black color.Benefits: This product offers excellent flame retardancy properties (UL 94, GWIT) combined with excellent processing, mechanical and electrical performance. Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This product is ideally suited for appliance and industrial control applications such as switches, timers and contactors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183/A
Water Absorption 0.80 %

@Temperature 23.0 °C,
Time 86400 sec
 0.80 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Viscosity 70 cP

@Shear Rate 100 1/s,
Temperature 300 °C
 70 cP

@Shear Rate 100 1/s,
Temperature 572 °F
105 cP

@Shear Rate 100 1/s,
Temperature 290 °C
 105 cP

@Shear Rate 100 1/s,
Temperature 554 °F
120 cP

@Shear Rate 100 1/s,
Temperature 280 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 536 °F
Linear Mold Shrinkage 0.0063 cm/cm
0.0063 in/in
Isotropy
Linear Mold Shrinkage, Flow >= 0.0060 cm/cm
>= 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0095 cm/cm
0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527 Type 1A
140 MPa
20300 psi
ASTM D638
Tensile Stress 45.0 MPa

@Strain 0.500 %
 6530 psi

@Strain 0.500 %
75.0 MPa

@Strain 1.50 %
 10900 psi

@Strain 1.50 %
80.0 MPa

@Strain 1.00 %
 11600 psi

@Strain 1.00 %
Elongation at Break 2.2 %
2.2 %
ISO 527 Type 1A
2.5 %
2.5 %
ASTM D638
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527 Type 1A
Flexural Strength 200 MPa
29000 psi
ISO 178
200 MPa
29000 psi
ASTM D790
Flexural Modulus 9.50 GPa
1380 ksi
ISO 178
9.50 GPa
1380 ksi
ASTM D790
Izod Impact, Notched 1.15 J/cm
2.15 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched 4.20 J/cm²
20.0 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.950 J/cm²
4.52 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ISO 75/Af
UL RTI, Electrical 130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 90.0 °C

@Thickness 0.750 mm
 194 °F

@Thickness 0.0295 in
100 °C

@Thickness 1.50 mm
 212 °F

@Thickness 0.0591 in
100 °C

@Thickness 3.00 mm
 212 °F

@Thickness 0.118 in
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 1210
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 1210
V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in
 1210
Oxygen Index 31 %
31 %
ISO 4589
Glow Wire Test 800 °C

@Thickness 0.800 mm
 1470 °F

@Thickness 0.0315 in
 ignition temperature; ISO 60695-2-13
825 °C

@Thickness 1.60 mm
 1520 °F

@Thickness 0.0630 in
 ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.3
3.3
IEC 60250
Dielectric Strength 42.0 kV/mm
1070 kV/in
IEC 60243
Dissipation Factor 0.010
0.010
IEC 60250
Comparative Tracking Index 400 V
400 V
Solution B; IEC 60112
450 V
450 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 270 - 280 °C
518 - 536 °F
Front Barrel Temperature 280 - 290 °C
536 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 275-285°C
Fire and smoke F index I3/F3
NF F 16 101
Mixing Zone 280-290°C