Polymer Property : Tensile Strength at Break = 140 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 140 MPa	<= 20300 psi	ISO/R527
Polykemi AB POLYshine PBT D221 GF30 PBT, Glass Fiber Reinforced Information provided by Polykemi AB
Tensile Strength at Break	<= 140 MPa	<= 20300 psi	ISO/R527
Polykemi AB SCANAMID 66 A53^ F43 Nylon 66, Glass Fiber Reinforced, Modified Information provided by Polykemi AB
Tensile Strength at Break	140 MPa	20300 psi
Radici Radilon® A RV300RKC (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength at Break	140 MPa @Temperature 23.0 °C	20300 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Crastin® SK608 BK509 PBT (Unverified Data**) Crastin® SK608 BK509 is a 45% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength at Break	140 MPa	20300 psi	5mm/min; ISO 527-2/1A
Celanese VECTRA A700 LCP, 30% Specialty (Unverified Data**) Some conductivity. Suitable for electrostatic dissipation (ESD) applications. 30% glass reinforced.30% glass fiber, suitable for electrostatic dissipation (ESD)A three-zone screw evenly divided in..
Tensile Strength at Break	140 MPa	20300 psi	5mm/min; ISO 527-2/1A
Celanese VECTRA E130G LCP, 30% Glass Reinforced (Unverified Data**) 30% glass fiber filled/low injection pressureInformation provided by Celanese
Tensile Strength at Break	140 MPa	20300 psi	ISO 527-1/-2
DSM Akulon® K224-G8U (Cond.) 43% Glass Reinforced Nylon 6 (North America) (discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break	140 MPa	20300 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® A 218G1 V30 Black 34N PA66, 30% glass fiber, Conditioned Description: Polyamide 66, reinforced with 30% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. For 7..
Tensile Strength at Break	140 MPa	20300 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 246 V 30 PA6, 30% glass fiber, DRY Description: Polyamide PA6, reinforced with 30 % of glass fiber, high impact strength, for injection molding.Available in: Asia Pacific and North AmericaProduct Applications: Having good mechanical ..
Tensile Strength at Break	140 MPa	20300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Tensile Strength at Break	140 MPa	20300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific) Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Tensile Strength at Break	140 MPa	20300 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Tensile Strength at Break	140 MPa	20300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Tensile Strength at Break	140 MPa	20300 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006ESZ PA 66 LNP THERMOCOMP* RF006ESZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Tensile Strength at Break	140 MPa	20300 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF006ESZ PA 66 LNP THERMOCOMP* RF006ESZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Tensile Strength at Break	140 MPa	20300 psi	ASTM D638
A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET Information provided by A. Schulman.
Tensile Strength at Break	140 MPa	20300 psi	ISO 527-93
Wellman Wellamid® GFT33NO51-NBK2 33% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman.
Tensile Strength at Break	140 MPa	20300 psi	ASTM D638
A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET Information provided by A. Schulman.
Tensile Strength at Break	140 MPa	20300 psi	ASTM D638
A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	140 MPa	20300 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-15 S PA6-GF15 Product description: Grilon BG-15 S is a heat stabilized PA6 injection molding grade with 15% glass fibers. Grilon BG-15 S has the following important properties: Excellent surface finishEasy flowin..
Tensile Strength at Break	140 MPa	20300 psi	ISO 527-1/-2
DSM Stanyl® TW200F3 Nylon 46-15% Glass Reinforced (European Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Tensile Strength at Break	140 MPa	20300 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® FG77G33L NC010 Nylon 612 33% Glass Reinforced Polyamide 612 with Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Tensile Strength at Break	140 MPa	20300 psi	5 mm/min; ISO 527
Eurostar Starflam BFR460B PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam BFR460B is a Flame Retardant, Glass Fiber Reinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	140 MPa	20300 psi	5 mm/min; ISO 527
Eurostar Starflam RF0055E PA66/6, 25% Glass Filled, Injection Molded Starflam RF0055E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1005Z250EM)Information provided by Polym..
Tensile Strength at Break	140 MPa	20300 psi	ISO 527
Eurotec® Tecodur® PB70 GR40 NL100 PBT, 40% glass fiber reinforced, natural Information provided by Eurotec®
Tensile Strength at Break	140 MPa	20300 psi	Conditioned; ISO R 527
Addiplast Addinyl B2 ZV 50 Nylon 6, 50% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
Tensile Strength at Break	140 MPa	20300 psi	5mm/min; ISO 527-2/1A
Celanese Celstran® PP-GF40-0414 P10 PP, 40% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese
Tensile Strength at Break	140 MPa	20300 psi	5mm/min; ISO 527-2/1A
Celanese Celstran® PP-GF50-0403 P10/10 PP, 50% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese
Tensile Strength at Break	140 MPa	20300 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® A3 GF 15 (2418) PA 6.6 Dry, 15% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break	140 MPa	20300 psi	ISO 527-1/-2
Lanxess Pocan® B 3235 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding