Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 439 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 226 °C

@Thickness 3.20 mm
439 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East)
LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ASTM D648
Covestro Petlon® DP3-1027 Semi-Crystalline PET, 45% Glass Fiber  (discontinued **)
Characteristics: General Purpose: Good Strength, High Rigidity and Heat ResistanceApplications: Automotive Valve Covers, Pump Components and PulleysProcessing: Injection Molding (Melt Temperature: 4..
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
DIN 53461
Polyram PE322G22 PET, 22% Glass Fiber  (discontinued **)
22% Glass fiber reinforced, flame retardant PET for injection molding applications.Information provided by Polyram Ram On Ind.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C

@Thickness 3.20 mm
439 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66
LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C

@Thickness 3.20 mm
439 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Asia Pacific)
LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ISO 75-1,-2
Gromax CFG35-R113N1 Nylon 6 36% Glass Filled (Dry)
Information provided by Gromax Enterprises Corp.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ISO 75/Af
Solvay TECHNYL® A 30 H1 V30 PA66, 30% glass fiber, DRY
Description: TECHNYL® A 30H1 V30 is a brominated flame retardant polyamide 66, reinforced with 30% of glass fiber, for injection molding. This product is available in natural & black color.Benefi..
Deflection Temperature at 1.8 MPa (264 psi) 226 °C

@Thickness 3.20 mm
439 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66
LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp RF004S PA 66
LNP* Thermocomp* RF004S is a Nylon 6/6 containing Glass Fiber. Characteristics are Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66
LNP* THERMOCOMP* RF006EUC is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include Easy Molding, UV Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RFB44XE PA 66 (Europe-Africa-Middle East)
LNP* Thermocomp* RFB44XE is a compound based on Nylon 66 resin containing Glass Fiber, Glass Bead. Added features of this material include: Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C

@Thickness 3.20 mm
439 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66
LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ASTM D648
Plenco 6401 Phenolic, Granular, Compression Molded
PLENCO 06401 is a glass fiber and mineral filled two-stage phenolic molding compound. UL recognized under component file E40654. 06401 is available in black.Information supplied by Plenco.
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ASTM D648
Plenco 6553 Phenolic, Granular, Compression Molded
Two-Stage Phenolic. PLENCO 06553 is a phenolic molding compound, formulated specifically for automotive brake pistons. 06553 exhibits excellent dimensional stability, and resistance to brake fluids..
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ASTM D648
Plenco 1506 Polyester, Briquette, Injection Molded
PLENCO 01506 is a mineral and cellulose filled granular polyester molding compound, with glass fiber reinforcement for improved mechanical strength properties. 01506 offers excellent electrical prop..
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
ISO 75-1,-2
Gromax CFG35-R113N1 Nylon 6 36% Glass Filled (Conditioned)
Information provided by Gromax Enterprises Corp.