SABIC Innovative Plastics NORYL NH7010 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH7010 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* NH7010 resin is a modified PPE-PS blend that exhibits an excellent balance of non-halogenated flame retardance, high heat resistance, good flow, and low specifc gravity for light weight parts. The resin will be available in custom colors and is suitable for injection molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10.1 g/10 min @Load 5.00 kg, Temperature 300 °C |
10.1 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 300 °C |
10 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| 69.0 MPa | 10000 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 8.4 % | 8.4 % | 50 mm/min; ISO 527 |
| 41 % | 41 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.9 % | 4.9 % | 50 mm/min; ISO 527 |
| 5.2 % | 5.2 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.25 GPa | 326 ksi | 5 mm/min; ASTM D638 |
| 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 102 MPa | 14800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 109 MPa | 15800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.47 GPa | 358 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.52 GPa | 365 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.23 J/cm | 4.18 ft-lb/in | ASTM D256 |
| 0.890 J/cm @Temperature -30.0 °C |
1.67 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 38.0 J @Temperature 23.0 °C |
28.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 81.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 81.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 81.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 160 °C | 320 °F | Rate B/50; ASTM D1525 |
| 161 °C | 322 °F | Rate B/50; ISO 306 | |
| 162 °C | 324 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 4701R PC (Europe-Africa-Middle East)
- Polymer Resources TPSF-GP1 PBT, 30% Glass Reinforced Structural Foam Grade
- Overview of materials for Polycarbonate, High Heat
- Lubriplate Super HDS L0792 Motor Oil Motor Oil & Transmission Fluid
- Momentive Performance Materials FQE205U Heat Cured Fluorosilicone Rubber
- Lubrizol Estane® MVT 70AT3 Thermoplastic Polyurethane, Moisture Vapor Transmission
- BASF 2-Methyl Imidazole Flake
- PSM Industries Pacific Sintered Metals Invar FN-251-S Powdered Metal
- Micropol Isoplas P602 Crosslinkable Polyethylene
Copyright © lookpolymers.com All Rights Reserved