Material Notes:

NORYL GTX934 is an unfilled GTX grade with improved processability and heat ageing performance.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Density	1.09 g/cc	0.0394 lb/inÂ³	ISO 1183
Moisture Absorption	1.21 %	1.21 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	3.5 %	3.5 %	ISO 62
Linear Mold Shrinkage, Flow	0.016 - 0.020 cm/cm	0.016 - 0.020 in/in	on Tensile Bar; SABIC Method
	0.014 - 0.017 cm/cm @Thickness 3.20 mm	0.014 - 0.017 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.011 - 0.014 cm/cm @Thickness 3.20 mm	0.011 - 0.014 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	13 g/10 min @Load 5.00 kg, Temperature 280 Â°C	13 g/10 min @Load 11.0 lb, Temperature 536 Â°F	ASTM D1238
Melt Index of Compound	13 g/10 min @Load 5.00 kg, Temperature 280 Â°C	13 g/10 min @Load 11.0 lb, Temperature 536 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, H358/30	85.0 MPa	12300 psi	ISO 2039-1
Tensile Strength at Break	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D638
	55.0 MPa	7980 psi	50 mm/min; ISO 527
Tensile Strength, Yield	65.0 MPa	9430 psi	Type I, 50 mm/min; ASTM D638
	65.0 MPa	9430 psi	50 mm/min; ISO 527
Elongation at Break	25 %	25 %	50 mm/min; ISO 527
	60 %	60 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	4.5 %	4.5 %	50 mm/min; ISO 527
	5.0 %	5.0 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.30 GPa	334 ksi	50 mm/min; ASTM D638
	2.40 GPa	348 ksi	1 mm/min; ISO 527
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
	95.0 MPa	13800 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.20 GPa	319 ksi	2 mm/min; ISO 178
	2.35 GPa	341 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	2.20 J/cm	4.12 ft-lb/in	ASTM D256
	1.00 J/cm @Temperature -30.0 Â°C	1.87 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
Izod Impact, Notched (ISO)	20.0 kJ/mÂ²	9.52 ft-lb/inÂ²	80104; ISO 180/1A
	10.0 kJ/mÂ² @Temperature -30.0 Â°C	4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA
	1.00 J/cmÂ² @Temperature -30.0 Â°C	4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	60.0 J @Temperature 23.0 Â°C	44.3 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	75.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	41.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	80.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	44.4 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	70.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	38.9 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
	85.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	47.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Thermal Conductivity	0.230 W/m-K	1.60 BTU-in/hr-ftÂ²-Â°F	ISO 8302
Deflection Temperature at 0.46 MPa (66 psi)	190 Â°C	374 Â°F	Edgew 120104 sp=100mm; ISO 75/Be
	190 Â°C @Thickness 3.20 mm	374 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	200 Â°C	392 Â°F	Rate B/50; ISO 306
	205 Â°C	401 Â°F	Rate B/120; ISO 306
	205 Â°C	401 Â°F	Rate B/50; ASTM D1525
	250 Â°C	482 Â°F	Rate A/50; ISO 306

Descriptive Properties	Value	Comments
Ball Pressure Test, 125Â°C +/- 2Â°C	PASSES	IEC 60695-10-2