SABIC Innovative Plastics LNP THERMOTUF WF003I Polyester, TP
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF WF003I Polyester, TP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* WF003I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| 1.374 g/cc | 0.04964 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0095 cm/cm @Time 86400 sec |
0.0095 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ISO 527 |
| 79.0 MPa | 11500 psi | ASTM D638 | |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| 134 MPa | 19400 psi | ASTM D790 | |
| Flexural Modulus | 4.58 GPa | 664 ksi | ASTM D790 |
| 4.71 GPa | 683 ksi | ISO 178 | |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.20 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Covestro Texin® 5250 Thermoplastic Polyurethane, Polyether-based, Medical (discontinued **)
- LyondellBasell Aquathene® CM04482 Catalyst Masterbatch
- Greene Tweed Xycomp® 1001-01 PEEK, Carbon Fiber Filled
- Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours
- Shin-Etsu Silicones KF-9011 Fluid
- Cytec Thornel® T-40 12K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- Colorite Polymers 8011-Rad Radiopaque Vinyl Compound
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 440A, Hardened + 538°C Temper
- SABIC Innovative Plastics LNP VERTON RVN17SXS PA 66 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved