Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours

Category Metal , Superalloy , Iron Base
Manufacturer Haynes International, Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts and basket liners, muffles and retorts, heat treating fixtures, waste incinerators, radiant tubes, cast link belt pins, recuperators, and fluidized bed components.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.07 g/cc
0.292 lb/in³
at RT.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 760 MPa
110000 psi
Tensile Strength, Yield 350 MPa

@Strain 0.200 %
50800 psi

@Strain 0.200 %
Elongation at Break 35 %
35 %
in 1.4 inches
Modulus of Elasticity 197 GPa
28600 ksi
RT
128 GPa

@Temperature 1000 °C
18600 ksi

@Temperature 1830 °F
136 GPa

@Temperature 900 °C
19700 ksi

@Temperature 1650 °F
143 GPa

@Temperature 800 °C
20700 ksi

@Temperature 1470 °F
152 GPa

@Temperature 700 °C
22000 ksi

@Temperature 1290 °F
159 GPa

@Temperature 600 °C
23100 ksi

@Temperature 1110 °F
165 GPa

@Temperature 500 °C
23900 ksi

@Temperature 932 °F
174 GPa

@Temperature 400 °C
25200 ksi

@Temperature 752 °F
182 GPa

@Temperature 300 °C
26400 ksi

@Temperature 572 °F
188 GPa

@Temperature 200 °C
27300 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
28100 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 14.3 µm/m-°C

@Temperature 25.0 - 100 °C
7.94 µin/in-°F

@Temperature 77.0 - 212 °F
14.9 µm/m-°C

@Temperature 25.0 - 200 °C
8.28 µin/in-°F

@Temperature 77.0 - 392 °F
15.3 µm/m-°C

@Temperature 25.0 - 300 °C
8.50 µin/in-°F

@Temperature 77.0 - 572 °F
15.8 µm/m-°C

@Temperature 25.0 - 400 °C
8.78 µin/in-°F

@Temperature 77.0 - 752 °F
16.1 µm/m-°C

@Temperature 25.0 - 500 °C
8.94 µin/in-°F

@Temperature 77.0 - 932 °F
16.4 µm/m-°C

@Temperature 25.0 - 600 °C
9.11 µin/in-°F

@Temperature 77.0 - 1110 °F
16.9 µm/m-°C

@Temperature 25.0 - 700 °C
9.39 µin/in-°F

@Temperature 77.0 - 1290 °F
17.3 µm/m-°C

@Temperature 25.0 - 800 °C
9.61 µin/in-°F

@Temperature 77.0 - 1470 °F
17.6 µm/m-°C

@Temperature 25.0 - 900 °C
9.78 µin/in-°F

@Temperature 77.0 - 1650 °F
17.8 µm/m-°C

@Temperature 25.0 - 1000 °C
9.89 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.467 J/g-°C
0.112 BTU/lb-°F
RT
0.483 J/g-°C

@Temperature 100 °C
0.115 BTU/lb-°F

@Temperature 212 °F
0.500 J/g-°C

@Temperature 200 °C
0.120 BTU/lb-°F

@Temperature 392 °F
0.522 J/g-°C

@Temperature 300 °C
0.125 BTU/lb-°F

@Temperature 572 °F
0.531 J/g-°C

@Temperature 400 °C
0.127 BTU/lb-°F

@Temperature 752 °F
0.558 J/g-°C

@Temperature 500 °C
0.133 BTU/lb-°F

@Temperature 932 °F
0.607 J/g-°C

@Temperature 600 °C
0.145 BTU/lb-°F

@Temperature 1110 °F
0.647 J/g-°C

@Temperature 700 °C
0.155 BTU/lb-°F

@Temperature 1290 °F
0.655 J/g-°C

@Temperature 800 °C
0.157 BTU/lb-°F

@Temperature 1470 °F
0.660 J/g-°C

@Temperature 900 °C
0.158 BTU/lb-°F

@Temperature 1650 °F
0.663 J/g-°C

@Temperature 1000 °C
0.158 BTU/lb-°F

@Temperature 1830 °F
0.667 J/g-°C

@Temperature 1100 °C
0.159 BTU/lb-°F

@Temperature 2010 °F
0.671 J/g-°C

@Temperature 1200 °C
0.160 BTU/lb-°F

@Temperature 2190 °F
Thermal Conductivity 11.4 W/m-K
79.1 BTU-in/hr-ft²-°F
RT
12.6 W/m-K

@Temperature 100 °C
87.4 BTU-in/hr-ft²-°F

@Temperature 212 °F
14.3 W/m-K

@Temperature 200 °C
99.2 BTU-in/hr-ft²-°F

@Temperature 392 °F
15.9 W/m-K

@Temperature 300 °C
110 BTU-in/hr-ft²-°F

@Temperature 572 °F
17.5 W/m-K

@Temperature 400 °C
121 BTU-in/hr-ft²-°F

@Temperature 752 °F
19.0 W/m-K

@Temperature 500 °C
132 BTU-in/hr-ft²-°F

@Temperature 932 °F
20.6 W/m-K

@Temperature 600 °C
143 BTU-in/hr-ft²-°F

@Temperature 1110 °F
22.2 W/m-K

@Temperature 700 °C
154 BTU-in/hr-ft²-°F

@Temperature 1290 °F
23.8 W/m-K

@Temperature 800 °C
165 BTU-in/hr-ft²-°F

@Temperature 1470 °F
25.4 W/m-K

@Temperature 900 °C
176 BTU-in/hr-ft²-°F

@Temperature 1650 °F
27.1 W/m-K

@Temperature 1000 °C
188 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1300 °C
2370 °F
Component Elements Properties Metric English Comments
Aluminum, Al 0.10 %
0.10 %
Boron, B 0.0040 %
0.0040 %
Carbon, C 0.050 %
0.050 %
Chromium, Cr 25 %
25 %
Cobalt, Co <= 3.0 %
<= 3.0 %
Iron, Fe 33 %
33 %
Manganese, Mn 0.70 %
0.70 %
Molybdenum, Mo <= 2.5 %
<= 2.5 %
Nickel, Ni 37 %
37 %
Niobium, Nb (Columbium, Cb) 0.70 %
0.70 %
Nitrogen, N 0.20 %
0.20 %
Silicon, Si 0.60 %
0.60 %
Tungsten, W <= 2.5 %
<= 2.5 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001052 ohm-cm
0.0001052 ohm-cm
RT
0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
0.0001245 ohm-cm

@Temperature 800 °C
0.0001245 ohm-cm

@Temperature 1470 °F
0.0001257 ohm-cm

@Temperature 900 °C
0.0001257 ohm-cm

@Temperature 1650 °F
0.0001266 ohm-cm

@Temperature 1000 °C
0.0001266 ohm-cm

@Temperature 1830 °F
0.0001278 ohm-cm

@Temperature 1100 °C
0.0001278 ohm-cm

@Temperature 2010 °F
0.0001287 ohm-cm

@Temperature 1200 °C
0.0001287 ohm-cm

@Temperature 2190 °F