Polymer Property : Linear Mold Shrinkage, Flow = 0.0070 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Colorcomp D10009 PC LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Colorcomp D10009 PC (Asia Pacific) LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific) LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Europe-Africa-Middle East) LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL002P PC (Asia Pacific) LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DL002PC PC LNP* LUBRICOMP* DL002PC is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this grade are: Wear Resistant, Exceptional Processing, Clean Compound System.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific) LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DX96651 PC (Asia Pacific) LNP LUBRICOMP* DX96651 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY D2000 PC (Asia Pacific) LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubriloy D2000XXH PC LNP LUBRILOY* D2000XXH is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated, Healthcare.This data was supplied..
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON AX00756 ABS LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON DX96717C PC LNP STAT-KON* DX96717C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Thickness 6.40 mm	0.0070 - 0.0090 in/in @Thickness 0.252 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® TS4016 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS LNP THERMOCOMP* AH0230A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS LNP THERMOCOMP* AH0230A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Asia Pacific) LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Europe-Africa-Middle East) LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KFZ24XXP Acetal Copoly LNP* THERMOCOMP* KFZ24XXP is a compound based on Acetal Copolymer resin containing 20% Glass Fiber, 10% Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled, Inter..
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP UC008H PPA LNP THERMOCOMP* UC008H is a compound based on Polyphthalamide resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP UC008H PPA (Asia Pacific) LNP* THERMOCOMP* UC008H is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP UC008H PPA (Asia Pacific) LNP* THERMOCOMP* UC008H is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead.
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC LNP* THERMOCOMP* DB008ERP is a compound based on Polycarbonate resin containing 40% Glass Bead. Added features of this material include: Easy Molding, Mold Release.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific) LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Thermocomp UC008S PPA LNP* Thermocomp* UC008S is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for..
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp UC008S PPA LNP* Thermocomp* UC008S is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for..