Greene Tweed Xycomp® 1001-01 PEEK, Carbon Fiber Filled

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer Greene Tweed
Trade Name Xycomp®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Greene Tweed Xycomp® 1001-01 PEEK, Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Greene, Tweeds Xycomp® engineered components offer a wider range of benefits than conventional thermoset resin systems because they rely on thermoplastic resins for their matrix. With specific strength and specific stiffness values over 400 percent that of Titanium and superior chemical compatibility and fire resistance properties, Greene, Tweeds Xycomp composites deliver greater value. Like all Greene, Tweed products, Xycomp components reflect the combination of engineering expertise with customer specifications. Additional benefits offered by Xycomp include improved chemical resistance, increased impact, toughness and ductility, more complex single-mold components, excellent post-molding machinability, recyclability, and infinite shelf life. Information provided by Greene Tweed.
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.6 MPa
13000 psi
90°; RT
2070 MPa
300000 psi
0°; RT
Tensile Strength, Ultimate 386 MPa
56000 psi
Open Hole
Elongation at Break 0.88 %
0.88 %
90°; RT
1.45 %
1.45 %
0°; RT
Tensile Modulus 10.3 GPa
1500 ksi
90°; RT
138 GPa
20000 ksi
0°; RT
Flexural Strength 2000 MPa
290000 psi
0°; RT
Flexural Modulus 124 GPa
18000 ksi
0°; RT
Compressive Strength 324 MPa
47000 psi
Open Hole
1360 MPa

@Temperature 22.0 °C
197000 psi

@Temperature 71.6 °F
0°
Compressive Modulus 124 GPa
18000 ksi
0°; RT
Poissons Ratio 0.30
0.30
RT
Shear Modulus 5.65 GPa
820 ksi
In Plane
Shear Strength 186 MPa
27000 psi
In-Plane