SABIC Innovative Plastics LNP THERMOCOMP RF0059 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP RF0059 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* RF0059 is a compound based on Nylon 66 resin containing 25% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ASTM D792
Moisture Absorption 0.800 %
0.800 %
50% RH, 24 hrs; ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength at Break 124 MPa
18000 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ASTM D638
Tensile Modulus 11.03 GPa
1600 ksi
50 mm/min; ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
Flexural Modulus 10.27 GPa
1490 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.34 J/cm
4.38 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 29.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 260 °C

@Thickness 3.20 mm
 500 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 246 °C

@Thickness 3.20 mm
 475 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.70 mm
 V-0

@Thickness 0.0669 in
 UL 94 by SABIC-IP