Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
Polymer Resources PCSF-FRG30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade Polycarbonate, 30% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing con.. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear LNP* LUBRICOMP* OFL36 is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched (Europe-Africa-Middle East) LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS (Asia Pacific) LNP* Lubricomp* OFL36A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM CRS5711 PEI (Asia Pacific) 15% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon WC003 PBT (Europe-Africa-Middle East) LNP* Stat-kon* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-.. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON WC003 PBT (Europe-Africa-Middle East) LNP* Stat-kon* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF005S PA 6 (Asia Pacific) LNP* Thermocomp* PF005S is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ISO 527 |
SABIC Innovative Plastics LNP VERTON NV004E PC+ABS (Europe-Africa-Middle East) LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing Long Glass. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP NF0061 PC+ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* NF0061 is a compound based on PC+ABS resin containing Glass Fiber, Flame Retardant. Added features include : Flame Retardant. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
PlastxWorld CEVIAN® A2606 30% GF PA/ABS Alloy, DAM Property data is for dry as molded (DAM) samples.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
Chase Plastics CP Pryme® NN113L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON OE002 PPS (Asia Pacific) LNP* Stat-kon* OE002 is a compound based on Polyphenylene Sulfide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |