SABIC Innovative Plastics LNP Lubricomp IP003 PA6.12

Category	Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Lubricomp IP003 PA6.12.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* IP003 is a Nylon 6/12 base resin containing PTFE and Silicone.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.16 g/cc	1.16 g/cc	ASTM D 792
Density	1.16 g/cc	0.0419 lb/inÂ³	ISO 1183
Moisture Absorption at Equilibrium	0.020 %	0.020 %	23Â°C / 50% RH; ISO 62
	0.020 % @Time 86400 sec	0.020 % @Time 24.0 hour	50% RH; ASTM D 570
Linear Mold Shrinkage, Flow	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D 955
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D 955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	43.0 MPa	6240 psi	5 mm/min; ISO 527
	44.0 MPa	6380 psi	Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield	43.0 MPa	6240 psi	5 mm/min; ISO 527
	44.0 MPa	6380 psi	Type I, 5 mm/min; ASTM D 638
Elongation at Break	13.7 %	13.7 %	5 mm/min; ISO 527
	17.5 %	17.5 %	Type I, 5 mm/min; ASTM D 638
Elongation at Yield	13.7 %	13.7 %	5 mm/min; ISO 527
	17.3 %	17.3 %	Type I, 5 mm/min; ASTM D 638
Tensile Modulus	1.96 GPa	284 ksi	1 mm/min; ISO 527
	2.02 GPa	293 ksi	50 mm/min; ASTM D 638
Flexural Strength	62.0 MPa	8990 psi	ISO 178
Flexural Modulus	1.87 GPa	271 ksi	2 mm/min; ISO 178
	1.91 GPa	277 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	0.300 J/cm @Temperature 23.0 Â°C	0.562 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Unnotched	5.59 J/cm @Temperature 23.0 Â°C	10.5 ft-lb/in @Temperature 73.4 Â°F	ASTM D 4812
Izod Impact, Notched (ISO)	3.00 kJ/mÂ² @Temperature 23.0 Â°C	1.43 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	28.0 kJ/mÂ² @Temperature 23.0 Â°C	13.3 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U
Impact Test	1.00 J @Temperature 23.0 Â°C	0.738 ft-lb @Temperature 73.4 Â°F	Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic	0.21	0.21	ASTM D 3702 Modified
Coefficient of Friction, Static	0.11	0.11	ASTM D 3702 Modified
K (wear) Factor	22.2 x 10^-8 mmÂ³/N-M	11.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D 3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	112 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	62.2 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D 696
CTE, linear, Transverse to Flow	127 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	70.6 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi)	146 Â°C	295 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	156 Â°C @Thickness 3.20 mm	313 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	61.0 Â°C	142 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	54.0 Â°C @Thickness 3.20 mm	129 Â°F @Thickness 0.126 in	unannealed; ASTM D 648