- SABIC Innovative Plastics LNP LUBRICOMP ZI001XXX PPE+PS (Asia Pacific)
SABIC Innovative Plastics LNP LUBRICOMP ZI001XXX PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ZI001XXX PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* ZI001XXX is a compound based on PPE+PS Blend resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0085 cm/cm @Time 86400 sec |
0.0085 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
| 51.0 MPa | 7400 psi | ASTM D638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ISO 527 |
| 43.0 MPa | 6240 psi | ASTM D638 | |
| Elongation at Break | 35.7 % | 35.7 % | ASTM D638 |
| 44.7 % | 44.7 % | ISO 527 | |
| Elongation at Yield | 2.3 % | 2.3 % | ISO 527 |
| 2.7 % | 2.7 % | ASTM D638 | |
| Tensile Modulus | 2.41 GPa | 350 ksi | 1 mm/min; ISO 527 |
| 2.75 GPa | 399 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 72.0 MPa | 10400 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| 2.75 GPa | 399 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.54 J/cm | 2.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.69 J/cm | 29.39 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 135 kJ/m² | 64.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded
- Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant
- Kraton® G1730 M (SEP) Linear Diblock Copolymer
- Saint-Gobain Quartzel® Fiber/Epoxy Resin Unidirectional Composite
- SABIC Innovative Plastics NORYL PX2637 PPE+HIPS (Asia Pacific)
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- CeramTec Rocar® S Silicon Carbide, SSiC
- Crucible Steel CSM® 6 Tool Steel, AISI A6
- ExxonMobil LLDPE LL 8446.21 Linear Low Density Polyethylene Resin (European Grade)
- Solvay RHODASURF® BC-840 Surfactant
Copyright © lookpolymers.com All Rights Reserved