SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA 6/10 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA 6/10 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* QCL349 is a compound based on Nylon 6/10 resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Internally Lubricated, Flame Retardant, Electrically Conductive.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ASTM D792
1.52 g/cc
0.0549 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 cm/cm

@Time 86400 sec
0.0010 in/in

@Time 24.0 hour
ASTM D955
0.0011 cm/cm

@Time 86400 sec
0.0011 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0078 cm/cm

@Time 86400 sec
0.0078 in/in

@Time 24.0 hour
ISO 294
0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 158 MPa
22900 psi
ASTM D638
162 MPa
23500 psi
ISO 527
Tensile Strength, Yield 162 MPa
23500 psi
ISO 527
168 MPa
24400 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ISO 527
1.9 %
1.9 %
ASTM D638
Elongation at Yield 1.6 %
1.6 %
ISO 527
1.8 %
1.8 %
ASTM D638
Tensile Modulus 15.75 GPa
2284 ksi
1 mm/min; ISO 527
16.54 GPa
2399 ksi
50 mm/min; ASTM D638
Flexural Strength 239 MPa
34700 psi
ISO 178
241 MPa
35000 psi
ASTM D790
Flexural Modulus 13.0 GPa
1890 ksi
ISO 178
13.1 GPa
1900 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
2.95 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.34
0.34
ASTM D3702 Modified
Coefficient of Friction, Static 0.28
0.28
ASTM D3702 Modified
K (wear) Factor 894 x 10-8 mm³/N-M
444 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
57.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 19.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
19.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
11.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
217 °C

@Thickness 3.20 mm
423 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 198 °C
388 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
200 °C

@Thickness 3.20 mm
392 °F

@Thickness 0.126 in
unannealed; ASTM D648