SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass, PTFE. Added features of this material include: Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.65 g/cc	0.0596 lb/inÂ³	ASTM D792
	1.65 g/cc	0.0596 lb/inÂ³	ISO 1183
Moisture Absorption	0.160 %	0.160 %	50% RH, 24 hrs; ASTM D570
	0.290 %	0.290 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.014 cm/cm @Time 86400 sec	0.014 in/in @Time 24.0 hour	ASTM D955
	0.015 cm/cm @Time 86400 sec	0.015 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0129 cm/cm @Time 86400 sec	0.0129 in/in @Time 24.0 hour	ISO 294
	0.016 cm/cm @Time 86400 sec	0.016 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ISO 527
	56.0 MPa	8120 psi	ASTM D638
Tensile Strength, Yield	49.0 MPa	7110 psi	ISO 527
	56.0 MPa	8120 psi	ASTM D638
Elongation at Break	2.6 %	2.6 %	ASTM D638
	4.0 %	4.0 %	ISO 527
Elongation at Yield	2.3 %	2.3 %	ISO 527
	3.6 %	3.6 %	ASTM D638
Tensile Modulus	5.80 GPa	841 ksi	1 mm/min; ISO 527
	6.13 GPa	889 ksi	50 mm/min; ASTM D638
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
	92.0 MPa	13300 psi	ISO 178
Flexural Modulus	5.30 GPa	769 ksi	ASTM D790
	6.30 GPa	914 ksi	ISO 178
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	ASTM D256
Izod Impact, Unnotched	2.08 J/cm	3.90 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	3.00 kJ/mÂ²	1.43 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	17.0 kJ/mÂ²	8.09 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	9.00 J	6.64 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	2.00 J	1.48 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.50	0.50	ASTM D3702 Modified
Coefficient of Friction, Static	0.43	0.43	ASTM D3702 Modified
K (wear) Factor	1850 x 10^-8 mmÂ³/N-M	920 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	161 Â°C @Thickness 3.20 mm	322 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	147 Â°C	297 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	132 Â°C @Thickness 3.20 mm	270 Â°F @Thickness 0.126 in	unannealed; ASTM D648