Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 91.7 MPa | 13300 psi | |
Poco Graphite EDM-3 EDM Graphite POCO's EDM-3 is an isotropic Ultrafine grain graphite which offers high strength with outstanding wear and fine surface finish characteristics easily machined to thicknesses of .005 or less.Applicat.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CY6012 PC+ABS (Asia Pacific) Cycoloy* resin grade CY6012 is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant systems. Excellent impact/flow balance together with a UL-94 V0 & 5VB rating.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
SABIC Innovative Plastics Cycoloy® MC5400 PC+ABS (Asia Pacific) |
|||
Flexural Strength | 91.4 MPa | 13300 psi | ASTM D790 |
PolyOne Edgetek® XT XT-100-BU00 PC+PBT
(discontinued **) EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of gen.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded
(discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti.. |
|||
Flexural Strength | <= 92.0 MPa | <= 13300 psi | ISO 178 |
Polykemi AB POLYshine PBT D201 T20 PBT, Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
Rostone Rosite® 4950BS SMC Thermoset Polyester, 10% Glass Reinforced
(discontinued **) Key Features: Low Shrink; Tight DimensionsRemarkable physical and electrical strength combined with excellent dimensional stability. Information provided by Oneida-Rostone Group. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
Kolon KOCETAL® DS500 Acid Resistant Acetal Resin Improved acid resistance. Applications: Products for improved chemical resistance. Information provided by API-Kolon. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer LNP LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer LNP LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), fo.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER (Europe-Africa-Middle East) Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), fo.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS LNP* THERMOCOMP* AX08306 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS (Asia Pacific) LNP* Thermocomp* AX08306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2mm/min; ISO 178 |
Teijin Panlite® LN-2250Y Flame Resistant, Translucent Polycarbonate Resin Flame retardant and mold release grade with normal fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications.Applications:Electric,.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL N300 PPE (Asia Pacific) High Heat 150deg.C, FR V-0 |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp LL003E PEEK LNP* Lubricomp* LL003E is a compound based on Polyetheretherketone (PEEK) containing PTFE. Characteristics of this grade are: Easy Molding and Internally Lubricated.This data was supplied by SABIC.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Europe-Afr.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
Flexural Strength | 92.0 MPa @Thickness 4.00 mm |
13300 psi @Thickness 0.157 in |
2.0 mm/min, Injection Molded; ISO 178 |
Styron EMERGEâ„¢ 7570 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS) Overview: EMERGEâ„¢ PC/ABS 7570 Advanced Resin is a high flow, ignition-resistant PC/ABS blend that contains now chlorinated or brominated additives. Its superior processing makes it ideal for in.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
Plenco 1501 Polyester, Briquette, Transfer Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
Chi Mei Kibisan® PN-107 L125 SAN High Clarity |
|||
Flexural Strength | 91.4 MPa | 13300 psi | ASTM D790 |
Entec Hyrene® PSCRY 2.5 General Purpose Polystyrene Available in North America Features: Crystal, General Purpose, and High Heat ResistanceRoHS Compliant Form: Pellets Information provided by Entec |
|||
Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
A. Schulman ComAlloy Lubrilon® 606 Nylon 6/6, PTFE Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Flexural Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Asia Pacific region. |