SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shielding and ESD.
Physical Properties Metric English Comments
Specific Gravity 1.33 g/cc
1.33 g/cc
ASTM D792
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0059 cm/cm

@Thickness 3.20 mm
0.0059 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12.3 g/10 min

@Load 5.00 kg,
Temperature 280 °C
12.3 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 31 g/10 min

@Load 10.0 kg,
Temperature 265 °C
31 g/10 min

@Load 22.0 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
5 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
5 mm/min; ISO 527
61.0 MPa
8850 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.7 %
3.7 %
Type I, 5 mm/min; ASTM D638
4.4 %
4.4 %
5 mm/min; ISO 527
Elongation at Yield 3.2 %
3.2 %
5 mm/min; ISO 527
3.4 %
3.4 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.00 GPa
435 ksi
1 mm/min; ISO 527
3.12 GPa
453 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
102 MPa
14800 psi
2 mm/min; ISO 178
Flexural Modulus 2.97 GPa
431 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.09 GPa
448 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.550 J/cm
1.03 ft-lb/in
ASTM D256
0.430 J/cm

@Temperature -30.0 °C
0.806 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 6.86 J/cm
12.9 ft-lb/in
ASTM D4812
5.88 J/cm

@Temperature -30.0 °C
11.0 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 39.0 kJ/m²
18.6 ft-lb/in²
80*10*4; ISO 180/1U
39.0 kJ/m²

@Temperature -30.0 °C
18.6 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
57.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 64.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
96.0 °C

@Thickness 3.20 mm
205 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 109 °C
228 °F
Rate B/50; ASTM D1525
109 °C
228 °F
Rate B/50; ISO 306
112 °C
234 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+7 ohm-cm
1.00e+7 ohm-cm
ASTM D257
Surface Resistance 1e+05
1e+05
ASTM D257
Shielding Effectiveness 47 dB

@Thickness 3.00 mm
47 dB

@Thickness 0.118 in
SABIC Method