Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 208 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ASTM D648
Plaskolite West Optix® CA-81 General Purpose Acrylic Resin
Extrusion Grade Pellets. Highest Molecular weight.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Polycasa Acryl® G 88 Acrylic
Glazing, domed roof lights, lighting covers, publicity lighting, reflectors, lenses, instrument covers, dishes and bowls; mostly used in the automotive industry.Data was collected by ISO methods.Qui..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
120°C/h; ISO 75/1
Polykemi AB POLYblend 65 M10 PC/ABS-blend, Reinforced
Information provided by Polykemi AB
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® MC1300 PC+ABS
Cycoloy MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Diameter 4.00 mm
208 °F

@Diameter 0.157 in
Unannealed; bar; ISO 75-2
NOVA Chemicals DYLARK® 480 Impact Grade Engineering Resin
Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Polycasa Acryl® G 88 E Acrylic
Same as Lucryl G 88, but higher resistance to stress cracking and higher processing viscosity. Used for: extruded protective layer on PVC, ABS and PC for outdoor applications, as well as bath tubs ..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Cycoloy® C6800 PC+ABS
PC+ABS, nonchlorinated, nonbrominated flame retardant.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 97.8 °C

@Thickness 6.35 mm
208 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Global GP-110 High Impact Polystyrene
High flowGood stiffnessApplications:AppliancesElectrical/Electronic applicationsHousehold goodsFood packagingToys
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Ineos ABS Lustran® H606 LS
Improved heat and UV resistance.,Property data per ISO test methods.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1,-2
Ineos ABS Lustran® Ultra 4000 PG ABS Pellets (a-methylstyrene-SAN-modified), Electroplating Grade
Lustran® Ultra 4000 PG is electroplating grade with high heat resistance. It is used for the production of molded plastic articles.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Asia Pacific)
LNP Lubricomp* KL004 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* Fu..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP KL004A Acetal Homopolymer
LNP LUBRICOMP* KL004A is a compound based on Acetal Homopolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 6.40 mm
208 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® 357U PBT (Asia Pacific)
Unreinforced PBTP, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant.
Deflection Temperature at 1.8 MPa (264 psi) 97.8 °C
208 °F
ASTM D648
Spartech Royalite R21 ABS General Purpose Sheet
Description: General Purpose SheetInformation provided by Spartech.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 6.40 mm
208 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Xenoy® 1101 PBT+PC (Asia Pacific)
Unreinforced, opaque polycarbonate/polyester alloy. Excellent low temperature impact plus chemical resistance to automotive fluid.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Xenoy® IQ4840 PBT+PC
Xenoy iQ4840 (PBT+PC) resin is an environmental responsible, sustainable, and low carbon footprint resin. It is a 10% mineral filled resin with high modulus and ductile (HMD) characteristics. Xen..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Xenoy® X4810 PBT+PC
Xenoy X4810 is a hydrostable, High Modulus Ductile PC/PBT blend. This resin provides low temperature (below 0C) ductile impact behaviour, high chemical resistance, very low creep, low CTE, excellent..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics XYLEX X8419 PC+POLYESTER (Europe-Africa-Middle East)
Low-medium flow, suitable for blow molding, injection molding, extrusion.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics XYLEX X8419 PC+POLYESTER (Europe-Africa-Middle East)
Low-medium flow, suitable for blow molding, injection molding, extrusion.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP AF006 ABS (Europe-Africa-Middle East)
LNP* Thermocomp* AF006 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ASTM D648
Samyang Trirex® DMH3000S Polycarbonate, High Flow Flame Retardancy
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.DMH3000S is a high flow, flame retardant grade.Applications: LCD TV Front cover, high ..
Deflection Temperature at 1.8 MPa (264 psi) 97.8 °C
208 °F
Annealed; ASTM Data
Styron Magnumâ„¢ 941 ABS
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Xenoy® X5601WX PBT + PC + PET
Impact modified PBT+PC+PET, Heat aging improved Xenoy
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP D452 PC COPOLYMER (Asia Pacific)
LNP* Thermocomp* D452 (or EXTC8202) is a compound based on SABIC unique Polycarbonate copolymer resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, ..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RW004 PA 66
LNP THERMOCOMP* RW004 is a compound based on Nylon 66 resin containing Wollastonite.
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1/-2
Covestro Bayblend® KU 1-1446* Polycarbonate + ABS
Developmental productGrade with improved low-temperature impact strength and petrol resistance for automotive partsin version BBS904 suitable for extrusion/extrusion blow molding and electroplating ..
Deflection Temperature at 1.8 MPa (264 psi) 97.8 °C
208 °F
ASTM D648
Evonik CYRO Acrylite® DQ 501 Compound Molding and Extrusion
ACRYLITE® SuPure™ acrylic polymer is an exceptional pure polymer designed for applications that demand maximum cleanliness. Our proprietary purification process starts at CYRO’s manufacturing pla..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
annealed; ISO 75
Chi Mei Polylac® PA-757 ABS
High gloss, medium impact
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1, -2
Celanese Celcon® LW90 POM, Tribological
Celcon« LW90 is a nominal 9 melt flow rate based material specifically formulated for high speed, low wear applications against metals. LW90 conforms to applicable FDA regulations governing food co..
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1, -2
Celanese Hostaform® LM90 POM, Specialty  (Unverified Data**)
Hostaform® LM90 is a nominal 9 melt flow rate acetal copolymer which is capable of being permanently marked by a laser. Parts molded from Hostaform® LM90 can be laser marked with barcodes, identif..