SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Heat Stabilized.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
1.38 g/cc
0.0499 lb/in³
ASTM D792
Moisture Absorption 0.530 %
0.530 %
50% RH, 24 hrs; ASTM D570
0.840 %
0.840 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm

@Time 86400 sec
0.0010 in/in

@Time 24.0 hour
ASTM D955
0.0011 cm/cm

@Time 86400 sec
0.0011 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Time 86400 sec
0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0072 cm/cm

@Time 86400 sec
0.0072 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
245 MPa
35500 psi
ISO 527
Elongation at Break 0.90 %
0.90 %
ASTM D638
1.8 %
1.8 %
ISO 527
Tensile Modulus 22.6 GPa
3280 ksi
1 mm/min; ISO 527
32.4 GPa
4700 ksi
50 mm/min; ASTM D638
Flexural Strength 372 MPa
54000 psi
ASTM D790
395 MPa
57300 psi
ISO 178
Flexural Modulus 18.4 GPa
2670 ksi
ASTM D790
22.7 GPa
3290 ksi
ISO 178
Izod Impact, Notched 1.01 J/cm
1.89 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.46 J/cm
19.60 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 68.0 kJ/m²
32.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.36
0.36
ASTM D3702 Modified
Coefficient of Friction, Static 0.30
0.30
ASTM D3702 Modified
K (wear) Factor 30.2 x 10-8 mm³/N-M
15.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 240 °C
>= 464 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
255 °C

@Thickness 3.20 mm
491 °F

@Thickness 0.126 in
unannealed; ASTM D648