SABIC Innovative Plastics Geloy XTWE280 ASA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy XTWE280 ASA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Weatherble ASA profile extrusion gradeThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D 792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.26 %
0.26 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.0 %

@Temperature 23.0 °C
1.0 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0052 - 0.0053 cm/cm

@Thickness 3.20 mm
0.0052 - 0.0053 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11 g/10 min

@Load 10.0 kg,
Temperature 220 °C
11 g/10 min

@Load 22.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
12 g/10 min

@Load 3.80 kg,
Temperature 200 °C
12 g/10 min

@Load 8.38 lb,
Temperature 392 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 33.0 MPa
4790 psi
Type I, 5 mm/min; ASTM D 638
37.0 MPa
5370 psi
5 mm/min; ISO 527
Tensile Strength, Yield 46.0 MPa
6670 psi
Type I, 5 mm/min; ASTM D 638
51.0 MPa
7400 psi
5 mm/min; ISO 527
Elongation at Break 13 %
13 %
Type I, 5 mm/min; ASTM D 638
31 %
31 %
5 mm/min; ISO 527
Elongation at Yield 2.8 %
2.8 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.70 GPa
392 ksi
5 mm/min; ASTM D 638
2.85 GPa
413 ksi
1 mm/min; ISO 527
Flexural Yield Strength 74.0 MPa
10700 psi
2 mm/min; ISO 178
78.0 MPa
11300 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.50 GPa
363 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.420 J/cm

@Temperature -30.0 °C
0.787 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
0.750 J/cm

@Temperature 23.0 °C
1.41 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
50.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
50.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
100 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C

@Thickness 3.20 mm
176 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 86.0 °C
187 °F
Rate B/50; ASTM D 1525
86.0 °C
187 °F
Rate B/50; ISO 306
88.0 °C
190 °F
Rate B/120; ISO 306